- Title
- Thermoluminescence of synthetic quartz annealed beyond its second phase inversion temperature
- Creator
- Mthwesi, Zuko
- ThesisAdvisor
- Chithambo, Makaiko L
- Date
- 2017
- Type
- Thesis
- Type
- Masters
- Type
- MSc
- Identifier
- http://hdl.handle.net/10962/46077
- Identifier
- vital:25577
- Description
- Thermoluminescence of synthetic quartz annealed at 1000 ºC for 10 minutes has been studied. The aim was to study mechanisms of thermoluminescence in annealed synthetic quartz and to discuss the results in terms of the physics of point defects. The sample was irradiated with a beta dose of 10 Gy of beta radiation and then heated at a linear heating rate of 1 ºC.s-1 up to 500 ºC. The thermoluminescence (TL) glow curve consists of three glow peaks. Peak I at 74 0C (main peak) with high intensity as compared to the other two peaks. Peak II at 144 ºC is more intense than peak III at 180 ºC. This study was on the main peak (MP) at 74 ºC and peak III at 180 ºC. Kinetic analysis was carried out to determine the trap depth E, frequency factor s and the order of kinetics b of both peaks using the initial rise, peak shape, variable heating rate, glow curve deconvolution and isothermal TL methods. The values of kinetic parameters obtained were around 0.7 to 1.0 eV for trap depth and in the interval of 108 to 1015 s-¹ for frequency factor for both peaks. The effect of heating rate from 0.5 to 5 ºC.s-¹ on the TL peak intensity and peak temperature was observed. Also the effect of thermal quenching was observed at high heating rates. Since the TL glow curve has overlapping TL peaks, the Tm-Tstop method from 54 ºC up to 64 ºC and E -Tstop methods were introduced where a first order single peak was observed. Phototransfered thermoluminescence (PTTL) was investigated and characterized by three peaks. First PTTL peak I at 72 ºC, peak II at 134 ºC and peak III at 176 ºC. Analysis was carried out on peaks I and III for the effect of dose dependence from 20-200 Gy. Thermal fading was observed on PTTL peaks I and III, after storage time of 30 minutes.
- Format
- 93 leaves, pdf
- Publisher
- Rhodes University, Faculty of Science, Physics and Electronics
- Language
- English
- Rights
- Mthwesi, Zuko
- Hits: 574
- Visitors: 660
- Downloads: 138
Thumbnail | File | Description | Size | Format | |||
---|---|---|---|---|---|---|---|
View Details Download | SOURCE1 | Adobe Acrobat PDF | 2 MB | Adobe Acrobat PDF | View Details Download |