The development of functionalized electrospun nanofibers for the control of pathogenic microorganisms in water.
- Authors: Kleyi, Phumelele Eldridge
- Date: 2014
- Subjects: Electrospinning , Nanofibers , Pathogenic microorganisms , Pathogenic microorganisms -- Detection , Drinking water -- Microbiology , Water quality -- Measurement , Imidazoles , Spectrum analysis , Anti-infective agents , Polymerization
- Language: English
- Type: Thesis , Doctoral , PhD
- Identifier: vital:4497 , http://hdl.handle.net/10962/d1013134
- Description: The thesis presents the development of functionalized electrospun nylon 6 nanofibers for the eradication of pathogenic microorganisms in drinking water. Imidazole derivatives were synthesized as the antimicrobial agents and were characterized by means of NMR spectroscopy, IR spectroscopy, elemental analysis and X-ray crystallography. The first set of compounds (2-substituted N-alkylimidazoles) consisted of imidazole derivatives substituted with different alkyl groups (methyl, ethyl, propyl, butyl, heptyl, octyl, decyl and benzyl) at the 1-position and various functional groups [carboxaldehyde (CHO), alcohol (CH2OH) and carboxylic acid (COOH)] at the 2-position. It was observed that the antimicrobial activity of the compounds increased with increasing alkyl chain length and decreasing pKa of the 2-substituent. It was also observed that the antimicrobial activity was predominantly against a Gram-positive bacterial strains [Staphylococcus aureus (MIC = 5-160 μg/mL) and Bacillus subtilis subsp. spizizenii (MIC = 5-20 μg/mL)], with the latter being the more susceptible. However, the compounds displayed poor antimicrobial activity against Gram-negative bacterial strain, E. coli (MIC = 150- >2500 μg/mL) and did not show any activity against the yeast, C. albicans. The second set of compounds consisted of the silver(I) complexes containing 2-hydroxymethyl-N-alkylimidazoles. The complexes displayed a broad spectrum antimicrobial activity towards the microorganisms that were tested and their activity [E. coli (MIC = 5-40 μg/mL), S. aureus (MIC = 20-80 μg/mL), Bacillus subtilis subsp. spizizenii (MIC = 5-40 μg/mL) and C. albicans (MIC = 40-80 μg/mL)] increased with the alkyl chain length of the 2-hydroxymethyl-N-alkylimidazole. The third set of compounds consisted of the vinylimidazoles containing the vinyl group either at the 1-position or at the 4- or 5- position. The imidazoles with the vinyl group at the 4- or 5-position contained the alkyl group (decyl) at the 1-position. For the fabrication of the antimicrobial nanofibers, the first two sets of imidazole derivatives (2-substituted N-alkylimidazoles and silver(I) complexes) were incorporated into electrospun nylon 6 nanofibers while the third set (2-substituted vinylimidazoles) was immobilized onto electrospun nylon 6 nanofibers employing the graft polymerization method. The antimicrobial nylon nanofibers were characterized by IR spectroscopy and SEM-EDAX (EDS). The electrospun nylon 6 nanofibers incorporated with 2-substituted N-alkylimidazoles displayed moderate to excellent levels of growth reduction against S. aureus (73.2-99.8 percent). For the electrospun nylon 6 nanofibers incorporated with silver(I) complexes, the levels of growth reduction were >99.99 percent, after the antimicrobial activity evaluation using the shake flask method. Furthermore, the grafted electrospun nylon 6 nanofibers showed excellent levels of growth reduction for E. coli (99.94-99.99 percent) and S. aureus (99.93-99.99 percent). The reusability results indicated that the grafted electrospun nylon 6 nanofibers maintained the antibacterial activity until the third cycle of useage. The cytotoxicity studies showed that grafted electrospun nylon 6 nanofibers possess lower cytotoxic effects on Chang liver cells with IC50 values in the range 23.48-26.81 μg/mL. The thesis demonstrated that the development of antimicrobial electrospun nanofibers, with potential for the eradication of pathogenic microoganisms in water, could be accomplished by incorporation as well as immobilization strategies.
- Full Text:
An ion imprinted polymer for the determination of Ni (II) ions from mine tailing samples
- Authors: Rammika, Modise
- Date: 2011
- Subjects: Imprinted polymers , Metal ions , Polymerization , Mineral industries -- Waste disposal
- Language: English
- Type: Thesis , Masters , MSc
- Identifier: vital:4323 , http://hdl.handle.net/10962/d1004981 , Imprinted polymers , Metal ions , Polymerization , Mineral industries -- Waste disposal
- Description: A Ni(II)-dimethylglyoxime ion imprinted polymer {Ni(II)-DMG IIP} was synthesized by the trapping method using the bulk polymerisation format. The structures of the imprinted and non-imprinted polymer were evaluated by infrared spectroscopy and the morphology was observed by scanning electron microscopy. The Ni(II)-DMG IIP was optimised for pH, mass, time and by the uniform design experimental method for the molar ratios of monomer to crosslinker to porogen and template to ligands as well as keeping these parameters constant and varying the quantities of initiator, 2,2'-azobisisobutyronitrile (AIBN). The optimum pH was 8.5, optimum mass was 50 mg, optimum time was 1 min and the optimum molar ratios of crosslinker to monomer, monomer to template and nickel(II) sulfate hexahydrate (NiSO₄.6H₂O) to 4-vinylpyridine to dimethylglyoxime were found to be 3.3:1.0, 0.6:1.0 and 1.0:0.6:3.6 respectively with 30 mg and 8 mL as the optimum amounts of initiator and porogen respectively. Through this optimisation, recovery of Ni(II) was increased from 98 to 100%. Selectivity of the ion imprinted polymer was evaluated by analysing, using an inductively coupled plasma-optical emission spectrometer, for Ni(II) ions that were spiked with varying concentrations of Co(II), Cu(II), Zn(II), Pd(II), Fe(II), Ca(II), Mg(II), Na(I) and K(I) in aqueous samples. Selectivity studies also confirmed that the ion imprinted polymer had very good selectivity characterised by % RSD of less than 5 %. Co(II) was the only ion found to slightly interfere with the determination of Ni(II). The limits of detection and quantification were found to be 3x10⁻⁴ μg/mL and 9x10⁻⁴ μg/mL respectively. The method was evaluated by a custom solution of ground water certified reference material (SEP-3) and sandy soil reference material (BCR-142R) and the concentrations of Ni(II) obtained were not significantly different to the certified ones. The Ni(II)-DMG IIP was then evaluated in aqueous and soil samples where recoveries of 93 to 100% and 98 to 99% respectively were obtained with enrichment factors ranging from 2 to 18 in aqueous and 27 to 40 in soil samples. Finally, the Ni(II)-DMG IIP was used to analyse mine tailings samples and Ni(II) recovery of 99% was obtained with an enrichment factor of 2.