List of Titles

Authors: Canlıca, Mevlüde , Coskun, Mustafa , Altındal, Ahmet , Nyokong, Tebello
Date: 2012
Subjects: To be catalogued
Language: English
Type: text , article
Identifier: http://hdl.handle.net/10962/245820 , vital:51408 , xlink:href="https://doi.org/10.1142/S1088424612500824"
Description: An Ag/Pc/p-Si Schottky barrier (SB) diode was fabricated. The current-voltage (I-V), capacitance-voltage (C-V) and conductance-voltage (G-V) measurements were carried out to determine the characteristic parameters such as barrier height, ideality factor and series resistance of the SB diode. The non-linear behavior of ln (I) vs. ln (V) and ln (I/V) vs. V1/2 plots indicated that the thermoionic emission theory can be applied to evaluate junction parameters for the investigated SB diode rather than space-charge limited conduction (SCLC) mechanism and bulk-limited Poole–Frenkel emission. The bulk doping concentration NB and fixed oxide charges Nf was determined from the measured high frequency C-V curve and was found to be 9.5 × 1014 cm-3 and 2.3 × 1013 cm-2, respectively. The values of barrier height obtained from Norde's function were compared with those from the forward bias current-voltage characteristic, and it was seen that there was a good agreement between barrier heights from both methods.
Full Text:
Date Issued: 2012

Authors: Canlıca, Mevlüde , Altındal, Ahmet , Nyokong, Tebello
Date: 2012
Subjects: To be catalogued
Language: English
Type: text , article
Identifier: http://hdl.handle.net/10962/243532 , vital:51161 , xlink:href="https://doi.org/10.1142/S1088424612500836"
Description: The synthesis of ball-type dinuclear Zn(II) phthalocyanine containing four 4,4′-(9H-fluorene-9,9-diyl)diphenol substituents at the non-peripheral position is presented. The structure of the synthesized compound was characterized using elemental analyzes, and UV-vis, FT-IR, 1H NMR and mass spectroscopies. The ΦF value was 0.16 and ΦT value was 0.72. The complex showed reasonably long triplet lifetimes with τT 7210 μs in DMSO. The frequency and temperature dependence of the dielectric properties of ZnPc were also investigated in the frequency range of 40–105 Hz and in the temperature range of 300–440 °K. It has been observed that both dielectric constant ε′ and dielectric loss ε″ decrease with the rise in frequency as they increase with the rise in temperature. The decrease in ε′ with increasing frequency is attributed to the fact that as the frequency increases, the polarizability contribution from orientation sources decreases and finally disappears.
Full Text:
Date Issued: 2012

Showing items 1 - 2 of 2