Temperature dependence of persistent luminescence in CaAl2O4: Eu2+, Nd3+ related to beta irradiation and optical excitation
- Kalita, Jitumani M, Chithambo, Makaiko L
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2019
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/105158 , vital:32470 , https://doi.org/10.1016/j.jlumin.2018.10.062
- Description: Mechanisms responsible for the emission of persistent luminescence in CaAl2O4:Eu2+,Nd3+ are typically studied following excitation by ultraviolet or visible light. In contrast, we have studied the persistent luminescence from this material after beta irradiation and optical excitation. These studies have been carried out at 25 °C as well as at various temperatures up to 100 °C. A thermoluminescence (TL) glow curve measured at 1 °C/s following beta irradiation showed a glow peak at 63 °C. On the other hand, a glow curve measured after 15 s of optical excitation by polychromatic white light shows a peak at 102 °C. The partial heating procedure reveals that each of the TL peaks consist of several overlapping components. The TL in each case was analysed for kinetic parameters. The initial rise analysis carried out on the rising edge of the overlapping components shows that the activation energy of the component peaks corresponding to beta irradiation is consistent at (0.59 ± 0.01) eV. In comparison, activation energies corresponding to optical excitation increases with the partial heating temperature from (0.71 ± 0.01) eV to (0.76 ± 0.01) eV. The activation energy of (0.59 ± 0.01) eV is ascribed to an oxygen vacancy whereas the range of activation energies between (0.71 ± 0.01) eV and (0.76 ± 0.01) eV is ascribed to the 4 f levels of the Nd dopant.
- Full Text: false
- Date Issued: 2019
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2019
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/105158 , vital:32470 , https://doi.org/10.1016/j.jlumin.2018.10.062
- Description: Mechanisms responsible for the emission of persistent luminescence in CaAl2O4:Eu2+,Nd3+ are typically studied following excitation by ultraviolet or visible light. In contrast, we have studied the persistent luminescence from this material after beta irradiation and optical excitation. These studies have been carried out at 25 °C as well as at various temperatures up to 100 °C. A thermoluminescence (TL) glow curve measured at 1 °C/s following beta irradiation showed a glow peak at 63 °C. On the other hand, a glow curve measured after 15 s of optical excitation by polychromatic white light shows a peak at 102 °C. The partial heating procedure reveals that each of the TL peaks consist of several overlapping components. The TL in each case was analysed for kinetic parameters. The initial rise analysis carried out on the rising edge of the overlapping components shows that the activation energy of the component peaks corresponding to beta irradiation is consistent at (0.59 ± 0.01) eV. In comparison, activation energies corresponding to optical excitation increases with the partial heating temperature from (0.71 ± 0.01) eV to (0.76 ± 0.01) eV. The activation energy of (0.59 ± 0.01) eV is ascribed to an oxygen vacancy whereas the range of activation energies between (0.71 ± 0.01) eV and (0.76 ± 0.01) eV is ascribed to the 4 f levels of the Nd dopant.
- Full Text: false
- Date Issued: 2019
The influence of dopants on thermoluminescence of Sr2MgSi2O7
- Thomas, Sunil, Kalita, Jitumani M, Chithambo, Makaiko L, Ntwaeaborwa, Odireleng M
- Authors: Thomas, Sunil , Kalita, Jitumani M , Chithambo, Makaiko L , Ntwaeaborwa, Odireleng M
- Date: 2019
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/105148 , vital:32469 , https://doi.org/10.1016/j.jlumin.2018.12.035
- Description: We report the influence of dopants on the thermoluminescence of Sr2MgSi2O7. Samples studied comprise undoped Sr2MgSi2O7 and doped versions, namely, Sr2MgSi2O7:Dy3+, Sr2MgSi2O7:Eu3+, Sr2MgSi2O7:Tb3+ and Sr2MgSi2O7:Tb3+,Eu3+ phosphors. All samples show a broad glow peak near 60 °C when measured at 1 °C/s after irradiation to 10 Gy. The peak changes with partial heating, irradiation and fades between irradiation and measurement in a manner expected of a composite one. The behaviour is used to exemplify the analysis of a composite peak on the basis that particular features reflect those of the dominant component.
- Full Text: false
- Date Issued: 2019
- Authors: Thomas, Sunil , Kalita, Jitumani M , Chithambo, Makaiko L , Ntwaeaborwa, Odireleng M
- Date: 2019
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/105148 , vital:32469 , https://doi.org/10.1016/j.jlumin.2018.12.035
- Description: We report the influence of dopants on the thermoluminescence of Sr2MgSi2O7. Samples studied comprise undoped Sr2MgSi2O7 and doped versions, namely, Sr2MgSi2O7:Dy3+, Sr2MgSi2O7:Eu3+, Sr2MgSi2O7:Tb3+ and Sr2MgSi2O7:Tb3+,Eu3+ phosphors. All samples show a broad glow peak near 60 °C when measured at 1 °C/s after irradiation to 10 Gy. The peak changes with partial heating, irradiation and fades between irradiation and measurement in a manner expected of a composite one. The behaviour is used to exemplify the analysis of a composite peak on the basis that particular features reflect those of the dominant component.
- Full Text: false
- Date Issued: 2019
Thermally and optically stimulated luminescence of natural red and blue corundum (Al2O3)
- Kalita, Jitumani M, Thomas, Sunil, Chithambo, Makaiko L
- Authors: Kalita, Jitumani M , Thomas, Sunil , Chithambo, Makaiko L
- Date: 2019
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/105177 , vital:32472 , https://doi.org/10.1016/j.jlumin.2018.09.058
- Description: We report the thermoluminescence (TL) and optically stimulated luminescence (OSL) of natural corundum (Al2O3) of two varieties; one red and the other blue. X-ray fluorescence spectroscopy of the samples show that the concentration of Al2O3 in the red corundum is 43.05% and 46.87% in the blue corundum. TL measurements carried out on un-annealed samples and samples annealed at 700 °C, 900 °C and 1200 °C show that the TL sensitivity increases with annealing. The sensitivity of the red corundum reaches a maximum after annealing at 900 °C whereas that of the blue corundum increases with annealing up to the maximum annealing temperature of 1200 °C used in this study. Both samples have a complex glow curve between 30 °C and 500 °C. The composite nature of the glow curves is deduced to be due to a continuum in the trap distribution in the crystal. The activation energy of the traps vary between 0.70 eV and 1.15 eV. The dose response of the red corundum under TL is linear within 100‒1000 Gy whereas that of the blue corundum is superlinear for the same dose range. The TL of both samples is reproducible but the signal fades with time between irradiation and measurement. Both samples produce OSL under 470 nm blue light stimulation. The dose response of the OSL is superlinear within 100‒1000 Gy. It is found that the samples also produce thermally-assisted OSL (TA-OSL) at elevated temperature. The TA-OSL intensity of the red corundum increases with dose up to 400 Gy and saturates thereafter. On the other hand, the intensity of the blue corundum increases consistently with dose from 100 Gy to 1000 Gy.
- Full Text: false
- Date Issued: 2019
- Authors: Kalita, Jitumani M , Thomas, Sunil , Chithambo, Makaiko L
- Date: 2019
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/105177 , vital:32472 , https://doi.org/10.1016/j.jlumin.2018.09.058
- Description: We report the thermoluminescence (TL) and optically stimulated luminescence (OSL) of natural corundum (Al2O3) of two varieties; one red and the other blue. X-ray fluorescence spectroscopy of the samples show that the concentration of Al2O3 in the red corundum is 43.05% and 46.87% in the blue corundum. TL measurements carried out on un-annealed samples and samples annealed at 700 °C, 900 °C and 1200 °C show that the TL sensitivity increases with annealing. The sensitivity of the red corundum reaches a maximum after annealing at 900 °C whereas that of the blue corundum increases with annealing up to the maximum annealing temperature of 1200 °C used in this study. Both samples have a complex glow curve between 30 °C and 500 °C. The composite nature of the glow curves is deduced to be due to a continuum in the trap distribution in the crystal. The activation energy of the traps vary between 0.70 eV and 1.15 eV. The dose response of the red corundum under TL is linear within 100‒1000 Gy whereas that of the blue corundum is superlinear for the same dose range. The TL of both samples is reproducible but the signal fades with time between irradiation and measurement. Both samples produce OSL under 470 nm blue light stimulation. The dose response of the OSL is superlinear within 100‒1000 Gy. It is found that the samples also produce thermally-assisted OSL (TA-OSL) at elevated temperature. The TA-OSL intensity of the red corundum increases with dose up to 400 Gy and saturates thereafter. On the other hand, the intensity of the blue corundum increases consistently with dose from 100 Gy to 1000 Gy.
- Full Text: false
- Date Issued: 2019
- «
- ‹
- 1
- ›
- »