Kinetic analysis and general features of thermoluminescence of B2O3-Li2O-ZnF2 glass
- Thomas, Sunil, Chithambo, Makaiko L
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116154 , vital:34324 , https://doi.org/10.1016/j.radmeas.2017.03.038
- Description: The intention of this study is to explore the thermoluminescence of beta irradiated B2O3-Li2O-ZnF2 glass. The glow-curve corresponding to 200 Gy shows three peaks; two weak-intensity peaks at 60 and 243 °C and a more prominent one at 118 °C, when measured at 1 °C/s. The dose response of the main peak at 118 °C was found to be sublinear in the range 200–1000 Gy. Regarding the kinetic analysis of the main peak, the activation energy of the corresponding electron trap was evaluated as 0.96 eV and the frequency factor as ∼1011 s−1. It is proposed that the thermoluminescence in B2O3-Li2O-ZnF2 glass is due to recombination of electrons, thermally released from Zn+ ionic defect sites, with the holes at boron-oxygen hole centres.
- Full Text: false
- Date Issued: 2017
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116154 , vital:34324 , https://doi.org/10.1016/j.radmeas.2017.03.038
- Description: The intention of this study is to explore the thermoluminescence of beta irradiated B2O3-Li2O-ZnF2 glass. The glow-curve corresponding to 200 Gy shows three peaks; two weak-intensity peaks at 60 and 243 °C and a more prominent one at 118 °C, when measured at 1 °C/s. The dose response of the main peak at 118 °C was found to be sublinear in the range 200–1000 Gy. Regarding the kinetic analysis of the main peak, the activation energy of the corresponding electron trap was evaluated as 0.96 eV and the frequency factor as ∼1011 s−1. It is proposed that the thermoluminescence in B2O3-Li2O-ZnF2 glass is due to recombination of electrons, thermally released from Zn+ ionic defect sites, with the holes at boron-oxygen hole centres.
- Full Text: false
- Date Issued: 2017
The influence of dose on the kinetic parameters and dosimetric features of the main thermoluminescence glow peak in α-Al2O3: C, Mg
- Kalita, Jitumani M, Chithambo, Makaiko L
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/119834 , vital:34787 , https://doi.org/10.1016/j.nimb.2016.12.027
- Description: The influence of dose (0.1–100 Gy) on the kinetic parameters and the dosimetric features of the main glow peak of α-Al2O3:C,Mg have been investigated. Thermoluminescence (TL) measured at 1 °C/s shows a very high intensity glow peak at 161 °C and six secondary peaks at 42, 72, 193, 279, 330, 370 °C respectively. Analysis shows that the main peak follows first order kinetics irrespective of the irradiation dose. The activation energy is found to be consistent at 1.37 eV and the frequency factor is of the order of 1014 s−1 for any dose between 0.1 and 100 Gy. Further, the analysis for thermal quenching of the main peak of 0.1 Gy irradiated sample shows that the activation energy for thermal quenching is (0.94 ± 0.04) eV.
- Full Text: false
- Date Issued: 2017
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/119834 , vital:34787 , https://doi.org/10.1016/j.nimb.2016.12.027
- Description: The influence of dose (0.1–100 Gy) on the kinetic parameters and the dosimetric features of the main glow peak of α-Al2O3:C,Mg have been investigated. Thermoluminescence (TL) measured at 1 °C/s shows a very high intensity glow peak at 161 °C and six secondary peaks at 42, 72, 193, 279, 330, 370 °C respectively. Analysis shows that the main peak follows first order kinetics irrespective of the irradiation dose. The activation energy is found to be consistent at 1.37 eV and the frequency factor is of the order of 1014 s−1 for any dose between 0.1 and 100 Gy. Further, the analysis for thermal quenching of the main peak of 0.1 Gy irradiated sample shows that the activation energy for thermal quenching is (0.94 ± 0.04) eV.
- Full Text: false
- Date Issued: 2017
Thermoluminescence of K-Mg-Al-Zn fluorophosphate glass
- Thomas, Sunil, Chithambo, Makaiko L
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/124188 , vital:35574 , https://doi.org/10.1016/j.optmat.2016.12.035
- Description: The thermoluminescence of beta irradiated K-Mg-Al-Zn fluorophosphate glass is reported. A glow-curve corresponding to 10 Gy measured at 1 °C/s shows two peaks, a weaker-intensity one at 70 °C and a more prominent one at 235 °C, the subject of this report. The main peak was observed to fade with delay between irradiation and measurement and specifically, by 11% in 15 h. Its dose response is superlinear in the dose range 1–190 Gy although the change was linear for the initial 10 Gy. Regarding kinetic analysis, the activation energy of the higher temperature peak was evaluated as 1.31 eV and that of the lower temperature peak was found as 0.47 eV. It was also noted that the main peak is affected by thermal quenching with an activation energy for thermal quenching equal to 1.37 eV. It is proposed that the mechanism associated with the thermoluminescence in K-Mg-Al-Zn fluorophosphate glass is that electrons trapped by the metal cations are released during heating and then recombine with holes at oxygen sites.
- Full Text: false
- Date Issued: 2017
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/124188 , vital:35574 , https://doi.org/10.1016/j.optmat.2016.12.035
- Description: The thermoluminescence of beta irradiated K-Mg-Al-Zn fluorophosphate glass is reported. A glow-curve corresponding to 10 Gy measured at 1 °C/s shows two peaks, a weaker-intensity one at 70 °C and a more prominent one at 235 °C, the subject of this report. The main peak was observed to fade with delay between irradiation and measurement and specifically, by 11% in 15 h. Its dose response is superlinear in the dose range 1–190 Gy although the change was linear for the initial 10 Gy. Regarding kinetic analysis, the activation energy of the higher temperature peak was evaluated as 1.31 eV and that of the lower temperature peak was found as 0.47 eV. It was also noted that the main peak is affected by thermal quenching with an activation energy for thermal quenching equal to 1.37 eV. It is proposed that the mechanism associated with the thermoluminescence in K-Mg-Al-Zn fluorophosphate glass is that electrons trapped by the metal cations are released during heating and then recombine with holes at oxygen sites.
- Full Text: false
- Date Issued: 2017
- «
- ‹