Adsorption and separation of platinum and palladium by polyamine functionalized polystyrene-based beads and nanofibers
- Fayemi, Omolola E, Ogunlaja, Adeniyi S, Kempgens, Pierre F M, Antunes, Edith M, Torto, Nelson, Nyokong, Tebello, Tshentu, Zenixole R
- Authors: Fayemi, Omolola E , Ogunlaja, Adeniyi S , Kempgens, Pierre F M , Antunes, Edith M , Torto, Nelson , Nyokong, Tebello , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241694 , vital:50961 , xlink:href="https://doi.org/10.1016/j.mineng.2013.06.006"
- Description: Adsorption and separation of platinum and palladium chlorido species (PtCl62- and PdCl42-) on polystyrene beads as well as nanofibers functionalized with ammonium centres based on ethylenediamine (EDA), diethylenetriamine (DETA), triethylenetetramine (TETA) and tris-(2-aminoethyl)amine (TAEA) are described. The functionalized sorbent materials were characterized by microanalysis, SEM, XPS, BET and FTIR. The surface area of the functionalized fibers was in the range 69–241 m2/g while it was 73–107 m2/g for the beads. The adsorption and loading capacities of the sorption materials were investigated using both the batch and column studies at 1 M HCl concentration. The adsorption studies for both PtCl62- and PdCl42- on the different sorbent materials fit the Langmuir isotherm with R2 values >0.99. The highest loading capacity of Pt and Pd were 7.4 mg/g and 4.3 mg/g respectively for the nanofiber sorbent material based on ethylenediamine (EDA) while the beads with ethylenediamine (EDA) gave 1.0 mg/g and 0.2 mg/g for Pt and Pd respectively. Metals loaded on the sorbent materials were recovered by using 3% m/v thiourea solution as the eluting agent with quantitative desorption efficiency under the selected experimental conditions. Separation of platinum from palladium was partially achieved by selective stripping of PtCl62- with 0.5 M of NaClO4 in 1.0 M HCl while PdCl42- was eluted with 0.5 M thiourea in 1.0 M HCl. Separation of platinum from iridium and rhodium under 1 M HCl concentration was successful on triethylenetriamine (TETA)-functionalized Merrifield beads. This material (M-TETA) showed selectivity for platinum albeit the low loading capacity.
- Full Text:
- Authors: Fayemi, Omolola E , Ogunlaja, Adeniyi S , Kempgens, Pierre F M , Antunes, Edith M , Torto, Nelson , Nyokong, Tebello , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241694 , vital:50961 , xlink:href="https://doi.org/10.1016/j.mineng.2013.06.006"
- Description: Adsorption and separation of platinum and palladium chlorido species (PtCl62- and PdCl42-) on polystyrene beads as well as nanofibers functionalized with ammonium centres based on ethylenediamine (EDA), diethylenetriamine (DETA), triethylenetetramine (TETA) and tris-(2-aminoethyl)amine (TAEA) are described. The functionalized sorbent materials were characterized by microanalysis, SEM, XPS, BET and FTIR. The surface area of the functionalized fibers was in the range 69–241 m2/g while it was 73–107 m2/g for the beads. The adsorption and loading capacities of the sorption materials were investigated using both the batch and column studies at 1 M HCl concentration. The adsorption studies for both PtCl62- and PdCl42- on the different sorbent materials fit the Langmuir isotherm with R2 values >0.99. The highest loading capacity of Pt and Pd were 7.4 mg/g and 4.3 mg/g respectively for the nanofiber sorbent material based on ethylenediamine (EDA) while the beads with ethylenediamine (EDA) gave 1.0 mg/g and 0.2 mg/g for Pt and Pd respectively. Metals loaded on the sorbent materials were recovered by using 3% m/v thiourea solution as the eluting agent with quantitative desorption efficiency under the selected experimental conditions. Separation of platinum from palladium was partially achieved by selective stripping of PtCl62- with 0.5 M of NaClO4 in 1.0 M HCl while PdCl42- was eluted with 0.5 M thiourea in 1.0 M HCl. Separation of platinum from iridium and rhodium under 1 M HCl concentration was successful on triethylenetriamine (TETA)-functionalized Merrifield beads. This material (M-TETA) showed selectivity for platinum albeit the low loading capacity.
- Full Text:
Catalytic oxidation of thioanisole using oxovanadium (IV)‐functionalized electrospun polybenzimidazole nanofibers
- Walmsley, Ryan S, Hlangothi, Percy, Litwinski, Christian, Nyokong, Tebello, Torto, Nelson, Tshentu, Zenixole R
- Authors: Walmsley, Ryan S , Hlangothi, Percy , Litwinski, Christian , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/242083 , vital:51000 , xlink:href="https://doi.org/10.1002/app.38067"
- Description: Polybenzimidazole fibers, with an average diameter of 262 nm, were produced by the process of electrospinning. These fibers were used as a solid support material for the immobilization of oxovanadium(IV) which was achieved via a reaction with vanadyl sulfate. The oxovanadium(IV)-functionalized nanofibers were used as heterogeneous catalysts for the oxidation of thioanisole under both batch and pseudo-continuous flow conditions with great success. Under batch conditions near quantitative oxidation of thioanisole was achieved in under 90 min, even after four successive catalytic reactions. Under continuous conditions, excellent conversion of thioanisole was maintained throughout the period studied at flow rates of up to 2 mLh−1. This study, therefore, proposes that electrospun polybenzimidazole nanofibers, with their small diameters, impressive chemical and thermal stability, as well as coordinating benzimidazole group, may be a desirable support material for immobilization of homogeneous catalysts.
- Full Text:
- Authors: Walmsley, Ryan S , Hlangothi, Percy , Litwinski, Christian , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/242083 , vital:51000 , xlink:href="https://doi.org/10.1002/app.38067"
- Description: Polybenzimidazole fibers, with an average diameter of 262 nm, were produced by the process of electrospinning. These fibers were used as a solid support material for the immobilization of oxovanadium(IV) which was achieved via a reaction with vanadyl sulfate. The oxovanadium(IV)-functionalized nanofibers were used as heterogeneous catalysts for the oxidation of thioanisole under both batch and pseudo-continuous flow conditions with great success. Under batch conditions near quantitative oxidation of thioanisole was achieved in under 90 min, even after four successive catalytic reactions. Under continuous conditions, excellent conversion of thioanisole was maintained throughout the period studied at flow rates of up to 2 mLh−1. This study, therefore, proposes that electrospun polybenzimidazole nanofibers, with their small diameters, impressive chemical and thermal stability, as well as coordinating benzimidazole group, may be a desirable support material for immobilization of homogeneous catalysts.
- Full Text:
Oxovanadium (IV)-containing poly (styrene-co-4′-ethenyl-2-hydroxyphenylimidazole) electrospun nanofibers for the catalytic oxidation of thioanisole
- Walmsley, Ryan S, Litwinski, Christian, Antunes, Edith M, Hlangothi, Percy, Hosten, Eric C, McCleland, Cedric, Nyokong, Tebello, Torto, Nelson, Tshentu, Zenixole R
- Authors: Walmsley, Ryan S , Litwinski, Christian , Antunes, Edith M , Hlangothi, Percy , Hosten, Eric C , McCleland, Cedric , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241665 , vital:50959 , xlink:href="https://doi.org/10.1016/j.molcata.2013.07.018"
- Description: The catalytic fibers have been fabricated by the electrospinning of a copolymer of styrene and 2-(2′-hydroxy-4′-ethenylphenyl)imidazole {p(ST-co-VPIM)} followed by a reaction with a methanolic vanadyl solution to afford the oxovanadium(IV)-containing poly(styrene-co-4′-ethenyl-2-hydroxyphenylimidazole) fibers {p(ST-co-VPIM)-VO fibers}. The relationship between polymer concentration and fiber diameter was investigated, and at high concentration (20 wt%) the fibers were quite large (average diameter of 3.8 μm) but as the concentration was reduced fibers of much lower diameter were produced (0.6 μm using 8 wt%). The BET surface area for p(ST-co-VPIM) fibers (0.6 μm diameter) was 47.9 m2 g−1 and functionalization of p(ST-co-VPIM) with vanadyl resulted in an increase in surface area to 60.7 m2 g−1 for p(ST-co-VPIM)-VO. The presence of vanadyl was confirmed by XPS and EPR. The EPR spectral analyses depicted complex speciation of vanadium within these polymer supports. These catalytic fibers were applied under batch and continuous flow conditions for the catalytic oxidation of thioanisole using hydrogen peroxide. The continuous flow method gave excellent and constant conversion throughout the 10 h period studied. The leaching of vanadium from the fiber support was 4% over the 10 h period indicating a significant stability of the material.
- Full Text:
- Authors: Walmsley, Ryan S , Litwinski, Christian , Antunes, Edith M , Hlangothi, Percy , Hosten, Eric C , McCleland, Cedric , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241665 , vital:50959 , xlink:href="https://doi.org/10.1016/j.molcata.2013.07.018"
- Description: The catalytic fibers have been fabricated by the electrospinning of a copolymer of styrene and 2-(2′-hydroxy-4′-ethenylphenyl)imidazole {p(ST-co-VPIM)} followed by a reaction with a methanolic vanadyl solution to afford the oxovanadium(IV)-containing poly(styrene-co-4′-ethenyl-2-hydroxyphenylimidazole) fibers {p(ST-co-VPIM)-VO fibers}. The relationship between polymer concentration and fiber diameter was investigated, and at high concentration (20 wt%) the fibers were quite large (average diameter of 3.8 μm) but as the concentration was reduced fibers of much lower diameter were produced (0.6 μm using 8 wt%). The BET surface area for p(ST-co-VPIM) fibers (0.6 μm diameter) was 47.9 m2 g−1 and functionalization of p(ST-co-VPIM) with vanadyl resulted in an increase in surface area to 60.7 m2 g−1 for p(ST-co-VPIM)-VO. The presence of vanadyl was confirmed by XPS and EPR. The EPR spectral analyses depicted complex speciation of vanadium within these polymer supports. These catalytic fibers were applied under batch and continuous flow conditions for the catalytic oxidation of thioanisole using hydrogen peroxide. The continuous flow method gave excellent and constant conversion throughout the 10 h period studied. The leaching of vanadium from the fiber support was 4% over the 10 h period indicating a significant stability of the material.
- Full Text:
The development of catalytic oxovanadium (IV)-containing microspheres for the oxidation of various organosulfur compounds
- Ogunlaja, Adeniyi S, Khene, Samson M, Antunes, Edith M, Nyokong, Tebello, Torto, Nelson, Tshentu, Zenixole R
- Authors: Ogunlaja, Adeniyi S , Khene, Samson M , Antunes, Edith M , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241783 , vital:50969 , xlink:href="https://doi.org/10.1016/j.apcata.2013.05.004"
- Description: The development of poly[allylSB-co-EGDMA] beads containing a tetradentate ligand was achieved via suspension polymerization. The catalyst poly[allylSB-co-EGDMA]-VO was synthesized by reacting VIVOSO4 with poly[allylSB-co-EGDMA]. XPS and EPR were used to confirm the presence of vanadium (V4+) on the beads. The synthesized catalyst (poly[allylSB-co-EGDMA]-VO) was found to have a BET surface area of 22 m2 g−1 and porosity of 135 Å, with the atomic force microscopy (AFM) showing more insight on the porous nature of the beads. Oxidation of thiophene (TH), benzothiophene (BT), dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) was carried out using tert-butyl hydroperoxide (t-BuOOH) as oxidant. An overall conversion of 60%, 82%, 98% and 87% was achieved for thiophene (TH), benzothiophene (BT), dibenzothiophene (DBT) and 4,6 dimethyldibenzothiophene (4,6-DMDBT) respectively at higher (t-BuOOH) to substrate ratio and at a temperature of 40 °C. The efficient oxidation of the various organosulfur compounds presents potential for the possible application of this catalyst in oxidative desulfurization (ODS) of crude oil.
- Full Text:
- Authors: Ogunlaja, Adeniyi S , Khene, Samson M , Antunes, Edith M , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241783 , vital:50969 , xlink:href="https://doi.org/10.1016/j.apcata.2013.05.004"
- Description: The development of poly[allylSB-co-EGDMA] beads containing a tetradentate ligand was achieved via suspension polymerization. The catalyst poly[allylSB-co-EGDMA]-VO was synthesized by reacting VIVOSO4 with poly[allylSB-co-EGDMA]. XPS and EPR were used to confirm the presence of vanadium (V4+) on the beads. The synthesized catalyst (poly[allylSB-co-EGDMA]-VO) was found to have a BET surface area of 22 m2 g−1 and porosity of 135 Å, with the atomic force microscopy (AFM) showing more insight on the porous nature of the beads. Oxidation of thiophene (TH), benzothiophene (BT), dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) was carried out using tert-butyl hydroperoxide (t-BuOOH) as oxidant. An overall conversion of 60%, 82%, 98% and 87% was achieved for thiophene (TH), benzothiophene (BT), dibenzothiophene (DBT) and 4,6 dimethyldibenzothiophene (4,6-DMDBT) respectively at higher (t-BuOOH) to substrate ratio and at a temperature of 40 °C. The efficient oxidation of the various organosulfur compounds presents potential for the possible application of this catalyst in oxidative desulfurization (ODS) of crude oil.
- Full Text:
A highly selective and sensitive pyridylazo-2-naphthol-poly (acrylic acid) functionalized electrospun nanofiber fluorescence “turn-off” chemosensory system for Ni 2+
- Adewuyi, Sheriff, Ondigo, Dezzline A, Zugle, Ruphino, Tshentu, Zenixole R, Nyokong, Tebello, Torto, Nelson
- Authors: Adewuyi, Sheriff , Ondigo, Dezzline A , Zugle, Ruphino , Tshentu, Zenixole R , Nyokong, Tebello , Torto, Nelson
- Date: 2012
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/246012 , vital:51428 , xlink:href="https://doi.org/10.1039/C2AY25182E"
- Description: A fluorescent nanofiber probe for the determination of Ni2+ was developed via the electrospinning of a covalently functionalized pyridylazo-2-naphthol-poly(acrylic acid) polymer. Fluorescent nanofibers with diameters in the range 230–800 nm were produced with uniformly dispersed fluorophores. The excitation and emission fluorescence were at wavelengths 479 and 557 nm respectively, thereby exhibiting a good Stokes' shift. This Ni2+ probe that employs fluorescence quenching in a solid receptor–fluorophore system exhibited a good correlation between the fluorescence intensity and nickel concentration up to 1.0 μg mL−1 based on the Stern–Volmer mechanism. The probe achieved a detection limit (3δ/S) of 0.07 ng mL−1 and a precision, calculated as a relative standard deviation (RSD) of more than 4% (n = 8). The concentration of Ni2+ in a certified reference material (SEP-3) was found to be 0.8986 μg mL−1, which is significantly comparable with the certified value of 0.8980 μg mL−1. The accuracy of the determinations, expressed as a relative error between the certified and the observed values of certified reference groundwater was ≤0.1%. The versatility of the nanofiber probe was demonstrated by affording simple, rapid and selective detection of Ni2+ in the presence of other competing metal ions by direct analysis, without employing any further sample handling steps.
- Full Text:
- Authors: Adewuyi, Sheriff , Ondigo, Dezzline A , Zugle, Ruphino , Tshentu, Zenixole R , Nyokong, Tebello , Torto, Nelson
- Date: 2012
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/246012 , vital:51428 , xlink:href="https://doi.org/10.1039/C2AY25182E"
- Description: A fluorescent nanofiber probe for the determination of Ni2+ was developed via the electrospinning of a covalently functionalized pyridylazo-2-naphthol-poly(acrylic acid) polymer. Fluorescent nanofibers with diameters in the range 230–800 nm were produced with uniformly dispersed fluorophores. The excitation and emission fluorescence were at wavelengths 479 and 557 nm respectively, thereby exhibiting a good Stokes' shift. This Ni2+ probe that employs fluorescence quenching in a solid receptor–fluorophore system exhibited a good correlation between the fluorescence intensity and nickel concentration up to 1.0 μg mL−1 based on the Stern–Volmer mechanism. The probe achieved a detection limit (3δ/S) of 0.07 ng mL−1 and a precision, calculated as a relative standard deviation (RSD) of more than 4% (n = 8). The concentration of Ni2+ in a certified reference material (SEP-3) was found to be 0.8986 μg mL−1, which is significantly comparable with the certified value of 0.8980 μg mL−1. The accuracy of the determinations, expressed as a relative error between the certified and the observed values of certified reference groundwater was ≤0.1%. The versatility of the nanofiber probe was demonstrated by affording simple, rapid and selective detection of Ni2+ in the presence of other competing metal ions by direct analysis, without employing any further sample handling steps.
- Full Text:
Imidazole-functionalized polymer microspheres and fibers–useful materials for immobilization of oxovanadium (IV) catalysts
- Walmsley, Ryan S, Ogunlaja, Adeniyi S, Coombes, Matthew J, Chidawanyika, Wadzanai J U, Litwinski, Christian, Torto, Nelson, Nyokong, Tebello, Tshentu, Zenixole R
- Authors: Walmsley, Ryan S , Ogunlaja, Adeniyi S , Coombes, Matthew J , Chidawanyika, Wadzanai J U , Litwinski, Christian , Torto, Nelson , Nyokong, Tebello , Tshentu, Zenixole R
- Date: 2012
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/246041 , vital:51431 , xlink:href="https://doi.org/10.1039/C2JM15485D"
- Description: Both polymer microspheres and microfibers containing the imidazole functionality have been prepared and used to immobilize oxovanadium(IV). The average diameters and BET surface areas of the microspheres were 322 μm and 155 m2 g−1 while the fibers were 1.85 μm and 52 m2 g−1, respectively. XPS and microanalysis confirmed the incorporation of imidazole and vanadium in the polymeric materials. The catalytic activity of both materials was evaluated using the hydrogen peroxide facilitated oxidation of thioanisole. The microspheres were applied in a typical laboratory batch reactor set-up and quantitative conversions (>99%) were obtained in under 240 min with turn-over frequencies ranging from 21.89 to 265.53 h−1, depending on the quantity of catalyst and temperature. The microspherical catalysts also proved to be recyclable with no drop in activity being observed after three successive reactions. The vanadium functionalized fibers were applied in a pseudo continuous flow set-up. Factors influencing the overall conversion and product selectivity, including flow rate and catalyst quantity, were investigated. At flow rates of 1–4 mL h−1 near quantitative conversion was maintained over an extended period. Keeping the mass of catalyst constant (0.025 g) and varying the flow rate from 1–6 mL h−1 resulted in a shift in the formation of the oxidation product methyl phenyl sulfone from 60.1 to 18.6%.
- Full Text:
- Authors: Walmsley, Ryan S , Ogunlaja, Adeniyi S , Coombes, Matthew J , Chidawanyika, Wadzanai J U , Litwinski, Christian , Torto, Nelson , Nyokong, Tebello , Tshentu, Zenixole R
- Date: 2012
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/246041 , vital:51431 , xlink:href="https://doi.org/10.1039/C2JM15485D"
- Description: Both polymer microspheres and microfibers containing the imidazole functionality have been prepared and used to immobilize oxovanadium(IV). The average diameters and BET surface areas of the microspheres were 322 μm and 155 m2 g−1 while the fibers were 1.85 μm and 52 m2 g−1, respectively. XPS and microanalysis confirmed the incorporation of imidazole and vanadium in the polymeric materials. The catalytic activity of both materials was evaluated using the hydrogen peroxide facilitated oxidation of thioanisole. The microspheres were applied in a typical laboratory batch reactor set-up and quantitative conversions (>99%) were obtained in under 240 min with turn-over frequencies ranging from 21.89 to 265.53 h−1, depending on the quantity of catalyst and temperature. The microspherical catalysts also proved to be recyclable with no drop in activity being observed after three successive reactions. The vanadium functionalized fibers were applied in a pseudo continuous flow set-up. Factors influencing the overall conversion and product selectivity, including flow rate and catalyst quantity, were investigated. At flow rates of 1–4 mL h−1 near quantitative conversion was maintained over an extended period. Keeping the mass of catalyst constant (0.025 g) and varying the flow rate from 1–6 mL h−1 resulted in a shift in the formation of the oxidation product methyl phenyl sulfone from 60.1 to 18.6%.
- Full Text:
Oxovanadium (IV)-catalysed oxidation of dibenzothiophene and 4, 6-dimethyldibenzothiophene
- Ogunlaja, Adeniyi S, Chidawanyika, Wadzanai J U, Antunes, Edith M, Fernandes, Manuel A, Nyokong, Tebello, Torto, Nelson, Tshentu, Zenixole R
- Authors: Ogunlaja, Adeniyi S , Chidawanyika, Wadzanai J U , Antunes, Edith M , Fernandes, Manuel A , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2012
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/246025 , vital:51429 , xlink:href="https://doi.org/10.1039/C2DT31433A"
- Description: The reaction between [VIVOSO4] and the tetradentate N2O2-donor Schiff base ligand, N,N-bis(o-hydroxybenzaldehyde)phenylenediamine (sal-HBPD), obtained by the condensation of salicylaldehyde and o-phenylenediamine in a molar ratio of 2 : 1 respectively, resulted in the formation of [VIVO(sal-HBPD)]. The molecular structure of [VIVO(sal-HBPD)] was determined by single crystal X-ray diffraction, and confirmed the distorted square pyramidal geometry of the complex with the N2O2 binding mode of the tetradentate ligand. The formation of the polymer-supported p[VIVO(sal-AHBPD)] proceeded via the nitrosation of sal-HBPD, followed by the reduction with hydrogen to form an amine group that was then linked to Merrifield beads followed by the reaction with [VIVOSO4]. XPS and EPR were used to confirm the presence of oxovanadium(IV) within the beads. The BET surface area and porosity of the heterogeneous catalyst p[VIVO(sal-AHBPD)] were found to be 6.9 m2 g−1 and 180.8 Å respectively. Microanalysis, TG, UV-Vis and FT-IR were used for further characterization of both [VIVO(sal-HBPD)] and p[VIVO(sal-AHBPD)]. Oxidation of dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) was investigated using [VIVO(sal-HBPD)] and p[VIVO(sal-AHBPD)] as catalysts. Progress for oxidation of these model compounds was monitored with a gas chromatograph fitted with a flame ionization detector. The oxidation products were characterized using gas chromatography-mass spectrometry, microanalysis and NMR. Dibenzothiophene sulfone (DBTO2) and 4,6-dimethyldibenzothiophene sulfone (4,6-DMDBTO2) were found to be the main products of oxidation. Oxovanadium(IV) Schiff base microspherical beads, p[VIVO(sal-AHBPD)], were able to catalyse the oxidation of sulfur in dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) to a tune of 88.0% and 71.8% respectively after 3 h at 40 °C. These oxidation results show promise for potential application of this catalyst in the oxidative desulfurization of crude oils.
- Full Text:
- Authors: Ogunlaja, Adeniyi S , Chidawanyika, Wadzanai J U , Antunes, Edith M , Fernandes, Manuel A , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2012
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/246025 , vital:51429 , xlink:href="https://doi.org/10.1039/C2DT31433A"
- Description: The reaction between [VIVOSO4] and the tetradentate N2O2-donor Schiff base ligand, N,N-bis(o-hydroxybenzaldehyde)phenylenediamine (sal-HBPD), obtained by the condensation of salicylaldehyde and o-phenylenediamine in a molar ratio of 2 : 1 respectively, resulted in the formation of [VIVO(sal-HBPD)]. The molecular structure of [VIVO(sal-HBPD)] was determined by single crystal X-ray diffraction, and confirmed the distorted square pyramidal geometry of the complex with the N2O2 binding mode of the tetradentate ligand. The formation of the polymer-supported p[VIVO(sal-AHBPD)] proceeded via the nitrosation of sal-HBPD, followed by the reduction with hydrogen to form an amine group that was then linked to Merrifield beads followed by the reaction with [VIVOSO4]. XPS and EPR were used to confirm the presence of oxovanadium(IV) within the beads. The BET surface area and porosity of the heterogeneous catalyst p[VIVO(sal-AHBPD)] were found to be 6.9 m2 g−1 and 180.8 Å respectively. Microanalysis, TG, UV-Vis and FT-IR were used for further characterization of both [VIVO(sal-HBPD)] and p[VIVO(sal-AHBPD)]. Oxidation of dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) was investigated using [VIVO(sal-HBPD)] and p[VIVO(sal-AHBPD)] as catalysts. Progress for oxidation of these model compounds was monitored with a gas chromatograph fitted with a flame ionization detector. The oxidation products were characterized using gas chromatography-mass spectrometry, microanalysis and NMR. Dibenzothiophene sulfone (DBTO2) and 4,6-dimethyldibenzothiophene sulfone (4,6-DMDBTO2) were found to be the main products of oxidation. Oxovanadium(IV) Schiff base microspherical beads, p[VIVO(sal-AHBPD)], were able to catalyse the oxidation of sulfur in dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) to a tune of 88.0% and 71.8% respectively after 3 h at 40 °C. These oxidation results show promise for potential application of this catalyst in the oxidative desulfurization of crude oils.
- Full Text:
Optimal template removal from molecularly imprinted polymers by pressurized hot water extraction
- Batlokwa, Bareki Shima, Mokgadi, Janes, Nyokong, Tebello, Torto, Nelson
- Authors: Batlokwa, Bareki Shima , Mokgadi, Janes , Nyokong, Tebello , Torto, Nelson
- Date: 2011
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/247813 , vital:51620 , xlink:href="https://doi.org/10.1007/s10337-010-1884-3"
- Description: An optimal extraction method for the removal of templates from molecularly imprinted polymers (MIPs) is presented. The extraction method is based on pressurized hot water extraction (PHWE). PHWE was evaluated by application to three distinctly colored MIPs for chlorophyll (green), quercetin (yellow) and phthalocynine (dark blue) with subsequent monitoring of template removal and template bleeding by an ultraviolet spectrophotometer. The templates were washed-off and the extraction efficiency (EE) was compared to that of soxhlet and ultrasonic extraction methods. PHWE employed hot water at an optimal temperature of 220 °C, pressure of 50 bars and flow rate of 2 mL min−1 to thoroughly wash-off the respective templates from their MIPs. The EE evaluated for PHWE was over 99.6% for all the MIPs with no subsequent or minimal template bleeding (more than 0.01%). The washing procedure was simple and relatively fast as it was achieved in 70 min at the most. At 95% confidence level (n = 3), soxhlet and ultrasonic recorded EE that was not significantly different (more than 94.5% in all cases) from that of PHWE (less than 99.6% in all cases). Soxhlet and ultrasonic had washing procedures that were slower (over 18 h) and employed large quantities (400 mL) of organic solvents modified with acids. The percentage relative standard deviations (%RSD) for the EE and recovery results were less than 2.3% in all cases indicating the high reproducibility of the method. Overall, the three methods performed comparably in extracting templates. PHWE seems to be the method of choice as it employed water which poses no environmental threat.
- Full Text:
- Authors: Batlokwa, Bareki Shima , Mokgadi, Janes , Nyokong, Tebello , Torto, Nelson
- Date: 2011
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/247813 , vital:51620 , xlink:href="https://doi.org/10.1007/s10337-010-1884-3"
- Description: An optimal extraction method for the removal of templates from molecularly imprinted polymers (MIPs) is presented. The extraction method is based on pressurized hot water extraction (PHWE). PHWE was evaluated by application to three distinctly colored MIPs for chlorophyll (green), quercetin (yellow) and phthalocynine (dark blue) with subsequent monitoring of template removal and template bleeding by an ultraviolet spectrophotometer. The templates were washed-off and the extraction efficiency (EE) was compared to that of soxhlet and ultrasonic extraction methods. PHWE employed hot water at an optimal temperature of 220 °C, pressure of 50 bars and flow rate of 2 mL min−1 to thoroughly wash-off the respective templates from their MIPs. The EE evaluated for PHWE was over 99.6% for all the MIPs with no subsequent or minimal template bleeding (more than 0.01%). The washing procedure was simple and relatively fast as it was achieved in 70 min at the most. At 95% confidence level (n = 3), soxhlet and ultrasonic recorded EE that was not significantly different (more than 94.5% in all cases) from that of PHWE (less than 99.6% in all cases). Soxhlet and ultrasonic had washing procedures that were slower (over 18 h) and employed large quantities (400 mL) of organic solvents modified with acids. The percentage relative standard deviations (%RSD) for the EE and recovery results were less than 2.3% in all cases indicating the high reproducibility of the method. Overall, the three methods performed comparably in extracting templates. PHWE seems to be the method of choice as it employed water which poses no environmental threat.
- Full Text:
Photophysical and photochemical behavior of electrospun fibers of a polyurethane polymer chemically linked to lutetium carboxyphenoxy phthalocyanine
- Zugle, Ruphino, Litwinski, Christian, Torto, Nelson, Nyokong, Tebello
- Authors: Zugle, Ruphino , Litwinski, Christian , Torto, Nelson , Nyokong, Tebello
- Date: 2011
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/248428 , vital:51685 , xlink:href="https://doi.org/10.1039/C1NJ20126C"
- Description: A phthalocyanine complex of lutetium substituted with four peripherally substituted 4-carboxyphenoxy groups was synthesized using cyclotetramerisation reaction. Its structure was elucidated using conventional spectroscopic methods and elemental analysis. The spectral behavior of the complex was studied in DMF solution and in a solid polyurethane fiber matrix. The UV-Visible spectrum showed a red shift in its Q-band maximum absorption within the fiber as compared to that in solution. The triplet quantum yield in DMF was determined to be 0.51 with a lifetime of 2.7 μs and a singlet oxygen quantum yield of 0.33 with a lifetime of 19.85 μs in the same solvent. The functionalized phthalocyanine fiber could be a promising fabric material for applications such as self-disinfecting in wound dressing. A method based on the conversion of ADMA was used to estimate the singlet oxygen quantum yield of the Pc in the hybrid fiber. An estimated singlet oxygen quantum yield value of 0.11 in aqueous medium was obtained. The fluorescence quantum yield of the Pc was found to be 0.01 with a lifetime of 3.20 ns in DMF.
- Full Text:
- Authors: Zugle, Ruphino , Litwinski, Christian , Torto, Nelson , Nyokong, Tebello
- Date: 2011
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/248428 , vital:51685 , xlink:href="https://doi.org/10.1039/C1NJ20126C"
- Description: A phthalocyanine complex of lutetium substituted with four peripherally substituted 4-carboxyphenoxy groups was synthesized using cyclotetramerisation reaction. Its structure was elucidated using conventional spectroscopic methods and elemental analysis. The spectral behavior of the complex was studied in DMF solution and in a solid polyurethane fiber matrix. The UV-Visible spectrum showed a red shift in its Q-band maximum absorption within the fiber as compared to that in solution. The triplet quantum yield in DMF was determined to be 0.51 with a lifetime of 2.7 μs and a singlet oxygen quantum yield of 0.33 with a lifetime of 19.85 μs in the same solvent. The functionalized phthalocyanine fiber could be a promising fabric material for applications such as self-disinfecting in wound dressing. A method based on the conversion of ADMA was used to estimate the singlet oxygen quantum yield of the Pc in the hybrid fiber. An estimated singlet oxygen quantum yield value of 0.11 in aqueous medium was obtained. The fluorescence quantum yield of the Pc was found to be 0.01 with a lifetime of 3.20 ns in DMF.
- Full Text:
- «
- ‹
- 1
- ›
- »