A comparative study of the dosimetric features of α-Al2O3: C, Mg and α-Al2O3: C
- Kalita, Jitumani M, Chithambo, Makaiko L
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/113058 , vital:33694 , https://doi.org/10.1093/rpd/ncx039
- Description: A comparative study of the dosimetric features of α-Al2O3:C,Mg and α-Al2O3:C relevant to thermoluminescence dosimetry is reported. A glow curve of α-Al2O3:C,Mg measured at 1°C/s after beta irradiation to 1 Gy shows two subsidiary peaks at 42°C (labelled as I) and 72°C (II) and the main peak at 161°C (III) whereas a glow curve of α-Al2O3:C measured under the same conditions shows the main peak at 178°C (II′) and a lower intensity peak at 48°C (I′). Apart from these ones, there are several other peaks at temperatures beyond that of the main peak in both α-Al2O3:C,Mg and α-Al2O3:C. However, the latter are not included in this study. We report a comparative quantitative analysis of dose response and fading of peaks I, II and III of α-Al2O3:C,Mg and peaks I′ and II′ of α-Al2O3:C. Analysis shows that the dose response of peaks I and III is sublinear within 1–10 Gy whereas that of peak II is superlinear within 1–4 Gy followed by a sublinear region within 4–10 Gy. In comparison, the dose response of peak I′ is superlinear within 1–4 Gy followed by a sublinear region within 4–10 Gy whereas that of peak II′ is sublinear within 1–4 Gy followed by a superlinear region within 4–10 Gy. As regards to fading corresponding to 1 Gy, peak I is very unstable and fades within 300 s, peak II is more stable and takes up to 43200 s to fade. In comparison, peak III fades down to 30% of its initial intensity within 2400 s. Interestingly, between 2400 and 800 s, the intensity fades by 17% only. Regarding fading in α-Al2O3:C, peak I′ fades within 600 s whereas peak II′ shows an inverse fading behaviour up to 64800 s. The rate of fading for peaks I, II and III in α-Al2O3:C,Mg was found to decrease with increase in dose. However, no such behaviour was observed in α-Al2O3:C. The fading in both samples is discussed on the basis of a charge hopping mechanism.
- Full Text:
- Date Issued: 2017
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/113058 , vital:33694 , https://doi.org/10.1093/rpd/ncx039
- Description: A comparative study of the dosimetric features of α-Al2O3:C,Mg and α-Al2O3:C relevant to thermoluminescence dosimetry is reported. A glow curve of α-Al2O3:C,Mg measured at 1°C/s after beta irradiation to 1 Gy shows two subsidiary peaks at 42°C (labelled as I) and 72°C (II) and the main peak at 161°C (III) whereas a glow curve of α-Al2O3:C measured under the same conditions shows the main peak at 178°C (II′) and a lower intensity peak at 48°C (I′). Apart from these ones, there are several other peaks at temperatures beyond that of the main peak in both α-Al2O3:C,Mg and α-Al2O3:C. However, the latter are not included in this study. We report a comparative quantitative analysis of dose response and fading of peaks I, II and III of α-Al2O3:C,Mg and peaks I′ and II′ of α-Al2O3:C. Analysis shows that the dose response of peaks I and III is sublinear within 1–10 Gy whereas that of peak II is superlinear within 1–4 Gy followed by a sublinear region within 4–10 Gy. In comparison, the dose response of peak I′ is superlinear within 1–4 Gy followed by a sublinear region within 4–10 Gy whereas that of peak II′ is sublinear within 1–4 Gy followed by a superlinear region within 4–10 Gy. As regards to fading corresponding to 1 Gy, peak I is very unstable and fades within 300 s, peak II is more stable and takes up to 43200 s to fade. In comparison, peak III fades down to 30% of its initial intensity within 2400 s. Interestingly, between 2400 and 800 s, the intensity fades by 17% only. Regarding fading in α-Al2O3:C, peak I′ fades within 600 s whereas peak II′ shows an inverse fading behaviour up to 64800 s. The rate of fading for peaks I, II and III in α-Al2O3:C,Mg was found to decrease with increase in dose. However, no such behaviour was observed in α-Al2O3:C. The fading in both samples is discussed on the basis of a charge hopping mechanism.
- Full Text:
- Date Issued: 2017
A study of the kinetics of a high temperature thermoluminescence peak in annealed natural quartz
- Thomas, Sunil, Chithambo, Makaiko L
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/110007 , vital:33213 , DOI: 10.1016/j.jlumin.2018.08.077
- Description: Thermoluminescence of a high temperature secondary glow-peak in natural quartz annealed at 900 °C is reported. The glow-curve of a sample irradiated to 10 Gy and measured at 1 °C/s shows three peaks; the main peak at 71 °C and two other weaker-intensity peaks at 125 °C and 177 °C. For reference, the peaks are labelled as I, II and III. This study is concerned with the secondary peak at 177 °C (peak III). The electron trap responsible for peak III is stable at ambient temperature as determined by monitoring the peak intensity after various delays between irradiation and measurement. The activation energy and frequency factor of the peak were estimated as ~1.24 eV and ~10¹² s⁻¹ respectively. The dose response of the peak in the range 1–300 Gy is sublinear. The influence of either partial heating or irradiation dose on the peak position suggest that the peak follows non-first-order kinetics.
- Full Text: false
- Date Issued: 2018
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/110007 , vital:33213 , DOI: 10.1016/j.jlumin.2018.08.077
- Description: Thermoluminescence of a high temperature secondary glow-peak in natural quartz annealed at 900 °C is reported. The glow-curve of a sample irradiated to 10 Gy and measured at 1 °C/s shows three peaks; the main peak at 71 °C and two other weaker-intensity peaks at 125 °C and 177 °C. For reference, the peaks are labelled as I, II and III. This study is concerned with the secondary peak at 177 °C (peak III). The electron trap responsible for peak III is stable at ambient temperature as determined by monitoring the peak intensity after various delays between irradiation and measurement. The activation energy and frequency factor of the peak were estimated as ~1.24 eV and ~10¹² s⁻¹ respectively. The dose response of the peak in the range 1–300 Gy is sublinear. The influence of either partial heating or irradiation dose on the peak position suggest that the peak follows non-first-order kinetics.
- Full Text: false
- Date Issued: 2018
Accuracy of the activation energy calculated from a thermoluminescence glow‐peak using a method that uses three points on the peak
- Ogundare, F O, Chithambo, Makaiko L
- Authors: Ogundare, F O , Chithambo, Makaiko L
- Date: 2006
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/123016 , vital:35397 , https://doi:10.1002/pssc.200521077
- Description: The utility of thermoluminescence (TL) in detecting changes in defect concentration in insulators is well established [1–3]. The underlying premise leading to the emission of TL is that exposure of a material to ionizing radiation causes a redistribution of charge in defect centres within the material. When the material is heated at a controlled linear rate, the thermoluminescence is emitted as a temperature-dependent set of peaks collectively known as a glow-curve. The shape and intensity of each of the glow-peaks may be characterized by a set of parameters consisting of the activation energy E, the frequency factors, the number of electrons n0 trapped in defect centres at the start of the heating, and the order of kinetics b. The order of kinetics b is an indication of the retrapping probability i.e. the probability that a free electron from the conduction band will be retrapped rather than recombine with a hole at a recombination centre to produce thermoluminescence. Retrapping of electrons reduces the TL intensity at any particular temperature during the heating process. The physical mechanisms of TL associated with a given glow curve are unique and may be characterized by analysis of the glow-curve for the said kinetic parameters.
- Full Text:
- Date Issued: 2006
- Authors: Ogundare, F O , Chithambo, Makaiko L
- Date: 2006
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/123016 , vital:35397 , https://doi:10.1002/pssc.200521077
- Description: The utility of thermoluminescence (TL) in detecting changes in defect concentration in insulators is well established [1–3]. The underlying premise leading to the emission of TL is that exposure of a material to ionizing radiation causes a redistribution of charge in defect centres within the material. When the material is heated at a controlled linear rate, the thermoluminescence is emitted as a temperature-dependent set of peaks collectively known as a glow-curve. The shape and intensity of each of the glow-peaks may be characterized by a set of parameters consisting of the activation energy E, the frequency factors, the number of electrons n0 trapped in defect centres at the start of the heating, and the order of kinetics b. The order of kinetics b is an indication of the retrapping probability i.e. the probability that a free electron from the conduction band will be retrapped rather than recombine with a hole at a recombination centre to produce thermoluminescence. Retrapping of electrons reduces the TL intensity at any particular temperature during the heating process. The physical mechanisms of TL associated with a given glow curve are unique and may be characterized by analysis of the glow-curve for the said kinetic parameters.
- Full Text:
- Date Issued: 2006
Characteristics of the thermoluminescence of Sm3+-doped P2O5-K2O-MgO-Al2O3-ZnF2 glass
- Thomas, Sunil, Chithambo, Makaiko L
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/109979 , vital:33211 , https://doi.org/10.1016/j.radmeas.2018.06.005
- Description: We report the thermoluminescence of Sm3+-doped P2O5-K2O-MgO-Al2O3-ZnF2 glass. A glow-curve measured at 1 °C/s after beta irradiation to 10 Gy shows two peaks; a broad high intensity one at 214.0 ± 0.4 °C and a weaker intensity peak at 75.2 ± 0.8 °C. The dependence of peak position on partial heating as well as on irradiation suggest that the main peak at 214 °C is a combination of several overlapping peaks. The activation energy of the different components of the main peak, calculated using the initial-rise method, differ showing that the components are distinct. The reproducibility, fading and dose response were examined by considering the dominant component of the main peak. The intensity of the peak changes with heating rate in a manner consistent with thermal quenching.
- Full Text: false
- Date Issued: 2018
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/109979 , vital:33211 , https://doi.org/10.1016/j.radmeas.2018.06.005
- Description: We report the thermoluminescence of Sm3+-doped P2O5-K2O-MgO-Al2O3-ZnF2 glass. A glow-curve measured at 1 °C/s after beta irradiation to 10 Gy shows two peaks; a broad high intensity one at 214.0 ± 0.4 °C and a weaker intensity peak at 75.2 ± 0.8 °C. The dependence of peak position on partial heating as well as on irradiation suggest that the main peak at 214 °C is a combination of several overlapping peaks. The activation energy of the different components of the main peak, calculated using the initial-rise method, differ showing that the components are distinct. The reproducibility, fading and dose response were examined by considering the dominant component of the main peak. The intensity of the peak changes with heating rate in a manner consistent with thermal quenching.
- Full Text: false
- Date Issued: 2018
Comprehensive kinetic analysis of thermoluminescence peaks of α-Al2O3: C, Mg
- Kalita, Jitumani M, Chithambo, Makaiko L
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116142 , vital:34323 , https://doi.org/10.1016/j.jlumin.2017.01.003
- Description: A comprehensive kinetic analysis of the glow peaks in α-Al2O3:C,Mg is reported. A thermoluminescence glow curve measured at 1 °C/s after beta irradiation to 1 Gy shows a high intensity peak hereafter referred to as the main peak at 161 °C and six lower intensity secondary peaks at 42, 72, 193, 279, 330, 370 °C respectively. For ease of reference, the secondary peaks are labelled as I, II, IV, V, VI and VII respectively and the main peak denoted peak III. Kinetic analysis of the glow peaks has been carried out using the initial rise, whole glow peak, peak shape, variable heating rate and glow curve deconvolution methods as well as by way of phosphorescence. Using Tm-Tstop, Tm-dose and phosphorescence analyses, the order of kinetics of the peaks has been evaluated as first order. Analysis by the peak shape, whole glow peak and deconvolution methods produce the same conclusion. The activation energy of peaks I through VII are calculated as ~0.83, 0.96, 1.37, 1.20, 1.15, 1.61 and 1.94 eV respectively. The frequency factors for all the peaks are of the order of 109 to 1014 s−1. The question of thermal quenching affecting the peaks was considered. The peaks III, IV and V, the only ones that could be conveniently studied in this regard, were found to be affected by thermal quenching. The activation energy for thermal quenching was calculated for peak III as 0.96±0.03 eV, for peak VI as 0.95±0.07 eV and for peak V as 1.26±0.08 eV. The thermal quenching phenomenon has been discussed with reference to F+ and F centres. An energy band model has been developed to discuss the luminescence mechanisms in α-Al2O3:C,Mg in light of finding in this work.
- Full Text: false
- Date Issued: 2017
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116142 , vital:34323 , https://doi.org/10.1016/j.jlumin.2017.01.003
- Description: A comprehensive kinetic analysis of the glow peaks in α-Al2O3:C,Mg is reported. A thermoluminescence glow curve measured at 1 °C/s after beta irradiation to 1 Gy shows a high intensity peak hereafter referred to as the main peak at 161 °C and six lower intensity secondary peaks at 42, 72, 193, 279, 330, 370 °C respectively. For ease of reference, the secondary peaks are labelled as I, II, IV, V, VI and VII respectively and the main peak denoted peak III. Kinetic analysis of the glow peaks has been carried out using the initial rise, whole glow peak, peak shape, variable heating rate and glow curve deconvolution methods as well as by way of phosphorescence. Using Tm-Tstop, Tm-dose and phosphorescence analyses, the order of kinetics of the peaks has been evaluated as first order. Analysis by the peak shape, whole glow peak and deconvolution methods produce the same conclusion. The activation energy of peaks I through VII are calculated as ~0.83, 0.96, 1.37, 1.20, 1.15, 1.61 and 1.94 eV respectively. The frequency factors for all the peaks are of the order of 109 to 1014 s−1. The question of thermal quenching affecting the peaks was considered. The peaks III, IV and V, the only ones that could be conveniently studied in this regard, were found to be affected by thermal quenching. The activation energy for thermal quenching was calculated for peak III as 0.96±0.03 eV, for peak VI as 0.95±0.07 eV and for peak V as 1.26±0.08 eV. The thermal quenching phenomenon has been discussed with reference to F+ and F centres. An energy band model has been developed to discuss the luminescence mechanisms in α-Al2O3:C,Mg in light of finding in this work.
- Full Text: false
- Date Issued: 2017
Dose response and kinetic analysis of thermoluminescence of Li–Zn fluoroborate glass
- Thomas, Sunil, Chithambo, Makaiko L
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116164 , vital:34326 , https://doi.org/10.1080/10420150.2017.1313844
- Description: The intention of this study is to explore the thermoluminescence properties of beta-irradiated Li–Zn fluoroborate glass. The glow-curve corresponding to 10 Gy shows two peaks when measured at 1°C/s. The dose response of the glass to beta irradiation was investigated. The trapping level parameters such as activation energy, frequency factor and order of kinetics associated with the observed glow-peak were determined using different methods. The thermoluminescence is affected by thermal quenching. A possible mechanism for the thermoluminescence is described.
- Full Text:
- Date Issued: 2017
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116164 , vital:34326 , https://doi.org/10.1080/10420150.2017.1313844
- Description: The intention of this study is to explore the thermoluminescence properties of beta-irradiated Li–Zn fluoroborate glass. The glow-curve corresponding to 10 Gy shows two peaks when measured at 1°C/s. The dose response of the glass to beta irradiation was investigated. The trapping level parameters such as activation energy, frequency factor and order of kinetics associated with the observed glow-peak were determined using different methods. The thermoluminescence is affected by thermal quenching. A possible mechanism for the thermoluminescence is described.
- Full Text:
- Date Issued: 2017
F-and F+-band radioluminescence and the influence of annealing on its emission spectra in Al2O3: C, Mg:
- Chithambo, Makaiko L, Kalita, Jitumani M, Finch, A A
- Authors: Chithambo, Makaiko L , Kalita, Jitumani M , Finch, A A
- Date: 2020
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/150130 , vital:38942 , https://doi.org/10.1016/j.radmeas.2020.106306
- Description: Radioluminescence spectra of Al2O3:C,Mg monitored at temperatures up to 400 °C is reported. Measurements were made on samples either as received or on ones annealed at 1200 °C. Radioluminescence is observed at 410 nm for the unannealed sample but principally at 330 and 410 nm in the annealed sample with the emission at 330 nm dominant. Both bands are subject to thermal quenching but the change for the F+ band is atypical. Temperature induced effects on these and other bands are discussed, as are complementary measurements of thermoluminescence spectra.
- Full Text:
- Date Issued: 2020
- Authors: Chithambo, Makaiko L , Kalita, Jitumani M , Finch, A A
- Date: 2020
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/150130 , vital:38942 , https://doi.org/10.1016/j.radmeas.2020.106306
- Description: Radioluminescence spectra of Al2O3:C,Mg monitored at temperatures up to 400 °C is reported. Measurements were made on samples either as received or on ones annealed at 1200 °C. Radioluminescence is observed at 410 nm for the unannealed sample but principally at 330 and 410 nm in the annealed sample with the emission at 330 nm dominant. Both bands are subject to thermal quenching but the change for the F+ band is atypical. Temperature induced effects on these and other bands are discussed, as are complementary measurements of thermoluminescence spectra.
- Full Text:
- Date Issued: 2020
Factors influencing the shape of CW-OSL signal obtained by stimulation of very deep traps in carbon-doped aluminium oxide: an experimental study
- Nyirenda, Angel N, Chithambo, Makaiko L
- Authors: Nyirenda, Angel N , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/115493 , vital:34149 , https://doi.org/10.1016/j.jlumin.2017.07.016
- Description: The optically stimulated luminescence from carbon-doped aluminium oxide (α-Al2O3:C) displays a peak with time under certain measurement conditions. In this paper, we present factors that influence the peak-like shape of continuous-wave optically stimulated luminescence (CW-OSL) signal. The report is based on the experimental study of OSL signals obtained by stimulation of very deep traps in α-Al2O3:C. Methods exploiting post-irradiation annealing, variable dose and temperature dependent OSL measurements were used in the investigation. It is found that the rising part of the CW-OSL peak is obtained when the rate of retrapping at the most optically active trap (main trap) exceeds the rate of direct radiative recombination following optical release of charges from all optically active traps. This is possible if, during optical stimulation, the primary trap responsible for OSL i.e. the main trap, is substantially unoccupied and the very deep, donor traps are substantially filled up. The rate of charge retrapping itself is deduced to depend on the occupancy of the acceptor traps i.e. shallow, main and secondary traps; concentration of charge carriers in the very deep, donor traps; the post-irradiation annealing temperature and the temperature at which the OSL is measured.
- Full Text: false
- Date Issued: 2017
- Authors: Nyirenda, Angel N , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/115493 , vital:34149 , https://doi.org/10.1016/j.jlumin.2017.07.016
- Description: The optically stimulated luminescence from carbon-doped aluminium oxide (α-Al2O3:C) displays a peak with time under certain measurement conditions. In this paper, we present factors that influence the peak-like shape of continuous-wave optically stimulated luminescence (CW-OSL) signal. The report is based on the experimental study of OSL signals obtained by stimulation of very deep traps in α-Al2O3:C. Methods exploiting post-irradiation annealing, variable dose and temperature dependent OSL measurements were used in the investigation. It is found that the rising part of the CW-OSL peak is obtained when the rate of retrapping at the most optically active trap (main trap) exceeds the rate of direct radiative recombination following optical release of charges from all optically active traps. This is possible if, during optical stimulation, the primary trap responsible for OSL i.e. the main trap, is substantially unoccupied and the very deep, donor traps are substantially filled up. The rate of charge retrapping itself is deduced to depend on the occupancy of the acceptor traps i.e. shallow, main and secondary traps; concentration of charge carriers in the very deep, donor traps; the post-irradiation annealing temperature and the temperature at which the OSL is measured.
- Full Text: false
- Date Issued: 2017
Features of an annealing-induced thermoluminescence peak in α-Al2O3: C, Mg
- Kalita, Jitumani M, Chithambo, Makaiko L
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116013 , vital:34289 , DOI: 10.1016/j.optmat.2017.05.034
- Description: We report the thermoluminescence glow curves of beta irradiated single crystal α-Al2O3:C,Mg after annealing at 700 and 900 °C. A glow curve measured at 1 °C/s from samples irradiated to 1 Gy following annealing at 700 and 900 °C shows a high intensity peak at 163 °C and seven secondary peaks of weaker intensity at 43, 73, 100, 195, 280, 329 and 370 °C. Comparing the position of the peaks in the annealed samples with those in an un-annealed one, it is observed that the peak at 100 °C appears only after annealing at and above 700 °C. Kinetic analysis of this annealing-induced peak was carried out using the initial rise, whole glow peak, peak shape, curve fitting and variable heating rate methods. The order of kinetics of the peak was determined as first order using various methods including the Tm-Tstop technique and the dependence of Tm on irradiation dose. The activation energy of the peak is about 1.01 eV and the frequency factor of the order of 1012 s−1. The peak was found to be affected by thermal quenching in analysis based on change of peak intensity with heating rate. The activation energy of thermal quenching was evaluated as 1.06 ± 0.08 eV. We speculate that the annealing-induced peak is due to formation of a new electron trap after destruction of the F22+(2 Mg) centre when the sample is annealed at 700 °C. The annealing-induced peak fades with storage between irradiation and measurement. It was also concluded that electrons from traps corresponding to secondary peaks get re-trapped at the main electron trap.
- Full Text: false
- Date Issued: 2017
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116013 , vital:34289 , DOI: 10.1016/j.optmat.2017.05.034
- Description: We report the thermoluminescence glow curves of beta irradiated single crystal α-Al2O3:C,Mg after annealing at 700 and 900 °C. A glow curve measured at 1 °C/s from samples irradiated to 1 Gy following annealing at 700 and 900 °C shows a high intensity peak at 163 °C and seven secondary peaks of weaker intensity at 43, 73, 100, 195, 280, 329 and 370 °C. Comparing the position of the peaks in the annealed samples with those in an un-annealed one, it is observed that the peak at 100 °C appears only after annealing at and above 700 °C. Kinetic analysis of this annealing-induced peak was carried out using the initial rise, whole glow peak, peak shape, curve fitting and variable heating rate methods. The order of kinetics of the peak was determined as first order using various methods including the Tm-Tstop technique and the dependence of Tm on irradiation dose. The activation energy of the peak is about 1.01 eV and the frequency factor of the order of 1012 s−1. The peak was found to be affected by thermal quenching in analysis based on change of peak intensity with heating rate. The activation energy of thermal quenching was evaluated as 1.06 ± 0.08 eV. We speculate that the annealing-induced peak is due to formation of a new electron trap after destruction of the F22+(2 Mg) centre when the sample is annealed at 700 °C. The annealing-induced peak fades with storage between irradiation and measurement. It was also concluded that electrons from traps corresponding to secondary peaks get re-trapped at the main electron trap.
- Full Text: false
- Date Issued: 2017
General features and kinetic analysis of thermoluminescence from annealed natural quartz
- Thomas, Sunil, Chithambo, Makaiko L
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/112885 , vital:33670 , https://doi.org/10.1016/j.jlumin.2018.02.003
- Description: The aim of this study is to explore the thermoluminescence properties of beta irradiated natural quartz annealed at 900 °C, that is, beyond its second phase inversion temperature of 867 °C. The sample was annealed to improve its sensitivity and to deplete any residual charge from electron traps. The glow-curve corresponding to 10 Gy shows three peaks when measured at 1 °C/s; a dominant one at 71 °C, the subject of this report, and two other ones at 125 and 177 °C. The dose response of the main peak was studied in the range 1–300 Gy. The activation energy of the main glow-peak was evaluated as ~1 eV. Kinetic analyses using various methods show that the main glow-peak follows first order kinetics.
- Full Text: false
- Date Issued: 2018
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/112885 , vital:33670 , https://doi.org/10.1016/j.jlumin.2018.02.003
- Description: The aim of this study is to explore the thermoluminescence properties of beta irradiated natural quartz annealed at 900 °C, that is, beyond its second phase inversion temperature of 867 °C. The sample was annealed to improve its sensitivity and to deplete any residual charge from electron traps. The glow-curve corresponding to 10 Gy shows three peaks when measured at 1 °C/s; a dominant one at 71 °C, the subject of this report, and two other ones at 125 and 177 °C. The dose response of the main peak was studied in the range 1–300 Gy. The activation energy of the main glow-peak was evaluated as ~1 eV. Kinetic analyses using various methods show that the main glow-peak follows first order kinetics.
- Full Text: false
- Date Issued: 2018
Influence of annealing on thermoluminescence of natural quartz: kinetic analysis and experimental study of apparent inverse thermal quenching
- Folley, Damilola E, Chithambo, Makaiko L
- Authors: Folley, Damilola E , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/109996 , vital:33212 , https://doi.org/10.1016/j.radmeas.2018.04.010
- Description: The influence of annealing on the main thermoluminescence glow-peak of natural quartz is reported. For comparison, results from un-annealed quartz are included. The glow-curve measured at 1 °Cs−1 after beta irradiation to 50 Gy revealed six peaks each for quartz annealed at 800 °C for 1 h and the un-annealed sample. The main peak in both quartzes was observed at 72 °C. This report focusses on kinetic analysis of the main peak. The analysis was carried out using various methods consisting of the initial rise, whole glow-peak, peak shape, variable heating rate and phosphorescence-based methods. The activation energy obtained using the various methods ranges between and for the annealed sample and between and for the un-annealed sample. The result suggests that annealing has little effect on the activation energy. The luminescence intensity decreased with heating rate in the un-annealed sample in a manner suggestive of thermal quenching. In contrast, the dependence of intensity on heating rate in the annealed sample is influenced by the dose the sample is irradiated to. Whereas thermal quenching was noted for a dose of 50 Gy in the un-annealed sample, the annealed sample showed evidence of thermal quenching at a low dose of 3 Gy with the opposite effect when irradiated to 50 Gy. The activation energies of thermal quenching were found as and for the un-annealed and annealed samples respectively. We ascribe the apparent dependence of thermal quenching on dose in the annealed sample to competition between radiative and non-radiative transitions at the recombination centre.
- Full Text: false
- Date Issued: 2018
- Authors: Folley, Damilola E , Chithambo, Makaiko L
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/109996 , vital:33212 , https://doi.org/10.1016/j.radmeas.2018.04.010
- Description: The influence of annealing on the main thermoluminescence glow-peak of natural quartz is reported. For comparison, results from un-annealed quartz are included. The glow-curve measured at 1 °Cs−1 after beta irradiation to 50 Gy revealed six peaks each for quartz annealed at 800 °C for 1 h and the un-annealed sample. The main peak in both quartzes was observed at 72 °C. This report focusses on kinetic analysis of the main peak. The analysis was carried out using various methods consisting of the initial rise, whole glow-peak, peak shape, variable heating rate and phosphorescence-based methods. The activation energy obtained using the various methods ranges between and for the annealed sample and between and for the un-annealed sample. The result suggests that annealing has little effect on the activation energy. The luminescence intensity decreased with heating rate in the un-annealed sample in a manner suggestive of thermal quenching. In contrast, the dependence of intensity on heating rate in the annealed sample is influenced by the dose the sample is irradiated to. Whereas thermal quenching was noted for a dose of 50 Gy in the un-annealed sample, the annealed sample showed evidence of thermal quenching at a low dose of 3 Gy with the opposite effect when irradiated to 50 Gy. The activation energies of thermal quenching were found as and for the un-annealed and annealed samples respectively. We ascribe the apparent dependence of thermal quenching on dose in the annealed sample to competition between radiative and non-radiative transitions at the recombination centre.
- Full Text: false
- Date Issued: 2018
Influence of argon-implantation on conventional and phototransferred thermoluminescence of synthetic quartz
- Nsengiyumva, S, Chithambo, Makaiko L, Pichon, L
- Authors: Nsengiyumva, S , Chithambo, Makaiko L , Pichon, L
- Date: 2016
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/124732 , vital:35656 , DOI: 10.1080/10420150.2016.1194412
- Description: Conventional and phototransferred thermoluminescence of crystalline synthetic quartz implanted with 70 keV Ar ions at fluences in the range 1 × 1014–5 × 1015 ions/cm2 is reported. The glow curves, recorded at 5°C/s from beta-irradiated samples of similar mass, show a prominent peak between 100°C and 120°C. The thermoluminescence intensity of all implanted samples was greater than that of the unimplanted one. The increase in sensitivity is attributed to a corresponding increase in the concentration of point defects, as a result of the implantation, which act as electron traps or recombination centres. Kinetic analysis carried out using the peak shape, whole glow-peak and curve-fitting methods produced values of the activation energy, frequency factor and order of kinetics that are generally independent of implantation fluence. This result suggests that implantation did not necessarily affect the nature of the electron traps. With respect to phototransferred thermoluminescence, it was observed that it only appeared in the sample implanted at the highest fluence of 5 × 1015 ions/cm2. This may be so because the concentration of deep traps produced as a result of implantation at low fluence is too low to give rise to phototransferred thermoluminescence. The intensity of the phototransferred thermoluminescence goes through a peak with illumination time. We attribute this behaviour to the relative concentration of holes at recombination centres and phototransferred electrons at shallow traps.
- Full Text: false
- Date Issued: 2016
- Authors: Nsengiyumva, S , Chithambo, Makaiko L , Pichon, L
- Date: 2016
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/124732 , vital:35656 , DOI: 10.1080/10420150.2016.1194412
- Description: Conventional and phototransferred thermoluminescence of crystalline synthetic quartz implanted with 70 keV Ar ions at fluences in the range 1 × 1014–5 × 1015 ions/cm2 is reported. The glow curves, recorded at 5°C/s from beta-irradiated samples of similar mass, show a prominent peak between 100°C and 120°C. The thermoluminescence intensity of all implanted samples was greater than that of the unimplanted one. The increase in sensitivity is attributed to a corresponding increase in the concentration of point defects, as a result of the implantation, which act as electron traps or recombination centres. Kinetic analysis carried out using the peak shape, whole glow-peak and curve-fitting methods produced values of the activation energy, frequency factor and order of kinetics that are generally independent of implantation fluence. This result suggests that implantation did not necessarily affect the nature of the electron traps. With respect to phototransferred thermoluminescence, it was observed that it only appeared in the sample implanted at the highest fluence of 5 × 1015 ions/cm2. This may be so because the concentration of deep traps produced as a result of implantation at low fluence is too low to give rise to phototransferred thermoluminescence. The intensity of the phototransferred thermoluminescence goes through a peak with illumination time. We attribute this behaviour to the relative concentration of holes at recombination centres and phototransferred electrons at shallow traps.
- Full Text: false
- Date Issued: 2016
Kinetic analysis and general features of thermoluminescence of B2O3-Li2O-ZnF2 glass
- Thomas, Sunil, Chithambo, Makaiko L
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116154 , vital:34324 , https://doi.org/10.1016/j.radmeas.2017.03.038
- Description: The intention of this study is to explore the thermoluminescence of beta irradiated B2O3-Li2O-ZnF2 glass. The glow-curve corresponding to 200 Gy shows three peaks; two weak-intensity peaks at 60 and 243 °C and a more prominent one at 118 °C, when measured at 1 °C/s. The dose response of the main peak at 118 °C was found to be sublinear in the range 200–1000 Gy. Regarding the kinetic analysis of the main peak, the activation energy of the corresponding electron trap was evaluated as 0.96 eV and the frequency factor as ∼1011 s−1. It is proposed that the thermoluminescence in B2O3-Li2O-ZnF2 glass is due to recombination of electrons, thermally released from Zn+ ionic defect sites, with the holes at boron-oxygen hole centres.
- Full Text: false
- Date Issued: 2017
- Authors: Thomas, Sunil , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116154 , vital:34324 , https://doi.org/10.1016/j.radmeas.2017.03.038
- Description: The intention of this study is to explore the thermoluminescence of beta irradiated B2O3-Li2O-ZnF2 glass. The glow-curve corresponding to 200 Gy shows three peaks; two weak-intensity peaks at 60 and 243 °C and a more prominent one at 118 °C, when measured at 1 °C/s. The dose response of the main peak at 118 °C was found to be sublinear in the range 200–1000 Gy. Regarding the kinetic analysis of the main peak, the activation energy of the corresponding electron trap was evaluated as 0.96 eV and the frequency factor as ∼1011 s−1. It is proposed that the thermoluminescence in B2O3-Li2O-ZnF2 glass is due to recombination of electrons, thermally released from Zn+ ionic defect sites, with the holes at boron-oxygen hole centres.
- Full Text: false
- Date Issued: 2017
On luminescence stimulated from deep traps using thermally-assisted time-resolved optical stimulation in α-Al2O3: C
- Nyirenda, Angel N, Chithambo, Makaiko L, Polymeris, G S
- Authors: Nyirenda, Angel N , Chithambo, Makaiko L , Polymeris, G S
- Date: 2016
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/124627 , vital:35639 , https://doi.org/10.1016/j.radmeas.2016.01.016
- Description: We report a study of charge transfer mechanisms of electrons stimulated optically from very deep traps, also known as donor traps, in α-Al2O3:C. The investigations were carried out using thermally-assisted time-resolved optical stimulation, thermoluminescence and by way of residual thermoluminescence from the main electron trap. When the charges are optically stimulated from the deep traps, they are redistributed via the conduction band to the main electron trap and the shallow trap from where they are optically or thermally released for recombination at luminescence centres. The luminescence is strongly quenched at high measurement temperature as evident by very short luminescence lifetimes at these temperatures. The main peak due to residual thermoluminescence is located at a higher temperature than the conventional main peak.
- Full Text: false
- Date Issued: 2016
- Authors: Nyirenda, Angel N , Chithambo, Makaiko L , Polymeris, G S
- Date: 2016
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/124627 , vital:35639 , https://doi.org/10.1016/j.radmeas.2016.01.016
- Description: We report a study of charge transfer mechanisms of electrons stimulated optically from very deep traps, also known as donor traps, in α-Al2O3:C. The investigations were carried out using thermally-assisted time-resolved optical stimulation, thermoluminescence and by way of residual thermoluminescence from the main electron trap. When the charges are optically stimulated from the deep traps, they are redistributed via the conduction band to the main electron trap and the shallow trap from where they are optically or thermally released for recombination at luminescence centres. The luminescence is strongly quenched at high measurement temperature as evident by very short luminescence lifetimes at these temperatures. The main peak due to residual thermoluminescence is located at a higher temperature than the conventional main peak.
- Full Text: false
- Date Issued: 2016
On the sensitivity of thermally and optically stimulated luminescence of α-Al2O3: C and α-Al2O3: C, Mg
- Kalita, Jitumani M, Chithambo, Makaiko L
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/119803 , vital:34784 , https://doi.org/10.1016/j.radmeas.2017.03.006
- Description: The luminescence sensitivity of α-Al2O3:C and α-Al2O3:C, Mg is of interest because of the contemporary use of these materials in dosimetry related applications. We report investigations concerning the change in sensitivity of thermoluminescence (TL) and optically stimulated luminescence (OSL) from α-Al2O3:C and α-Al2O3:C, Mg with re-use. The study was carried out on a set of un-annealed samples and others annealed at 700 and 900 °C. The TL and OSL sensitivity in α-Al2O3:C and α-Al2O3:C, Mg was found to increase with sample re-use whether the intensity was monitored as peak area or peak height for the main TL peak or, in the case of OSL, as the maximum intensity or the area under a decay curve. The fractional increase in area under either the main TL peak or the OSL decay curve exceeds that of the TL peak height or maximum OSL intensity when samples are re-used. However, when un-annealed samples are used, any increase in TL peak height or peak area per measurement is less than observed in annealed samples. It is also interesting to note that the change in maximum OSL intensity or OSL area is minimal for samples annealed at 900 °C. In general, the TL sensitivity in α-Al2O3:C increases more than that in α-Al2O3:C, Mg with re-use. On the other hand, the OSL sensitivity in α-Al2O3:C, Mg increases more than that in α-Al2O3:C with re-use. These findings suggest that it is advisable to take into account the fractional increase in sensitivity per measurement when one uses α-Al2O3:C as a TL dosimeter and α-Al2O3:C, Mg as an OSL dosimeter.
- Full Text: false
- Date Issued: 2017
- Authors: Kalita, Jitumani M , Chithambo, Makaiko L
- Date: 2017
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/119803 , vital:34784 , https://doi.org/10.1016/j.radmeas.2017.03.006
- Description: The luminescence sensitivity of α-Al2O3:C and α-Al2O3:C, Mg is of interest because of the contemporary use of these materials in dosimetry related applications. We report investigations concerning the change in sensitivity of thermoluminescence (TL) and optically stimulated luminescence (OSL) from α-Al2O3:C and α-Al2O3:C, Mg with re-use. The study was carried out on a set of un-annealed samples and others annealed at 700 and 900 °C. The TL and OSL sensitivity in α-Al2O3:C and α-Al2O3:C, Mg was found to increase with sample re-use whether the intensity was monitored as peak area or peak height for the main TL peak or, in the case of OSL, as the maximum intensity or the area under a decay curve. The fractional increase in area under either the main TL peak or the OSL decay curve exceeds that of the TL peak height or maximum OSL intensity when samples are re-used. However, when un-annealed samples are used, any increase in TL peak height or peak area per measurement is less than observed in annealed samples. It is also interesting to note that the change in maximum OSL intensity or OSL area is minimal for samples annealed at 900 °C. In general, the TL sensitivity in α-Al2O3:C increases more than that in α-Al2O3:C, Mg with re-use. On the other hand, the OSL sensitivity in α-Al2O3:C, Mg increases more than that in α-Al2O3:C with re-use. These findings suggest that it is advisable to take into account the fractional increase in sensitivity per measurement when one uses α-Al2O3:C as a TL dosimeter and α-Al2O3:C, Mg as an OSL dosimeter.
- Full Text: false
- Date Issued: 2017
Optically stimulated luminescence and spectral emission features of radioluminescence and thermoluminescence of natural kunzite:
- Alatishe, M A, Ogundare, F O, Folley, Damilola E, Chithambo, Makaiko L, Chikwembani, S
- Authors: Alatishe, M A , Ogundare, F O , Folley, Damilola E , Chithambo, Makaiko L , Chikwembani, S
- Date: 2020
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/160478 , vital:40449 , https://doi.org/10.1016/j.radmeas.2020.106457
- Description: Features of luminescence optically stimulated from natural kunzite using 470 nm blue light are reported. Preparatory measurements of its X-ray excited radioluminescence and thermoluminescence show that the sample has two main bands centered at 360 nm and 600 nm. The optically stimulated luminescence discussed in this report was monitored in the UV region and is presumed to be the same 360 nm emission that appears in the radioluminescence and thermoluminescence spectra. The glow curve shows at least three peaks at 74, 202, 432 oC for heating at 1 oC and the third one is a composite of two. Only the first two peaks are deduced to contribute most of the optically stimulated luminescence.
- Full Text:
- Date Issued: 2020
- Authors: Alatishe, M A , Ogundare, F O , Folley, Damilola E , Chithambo, Makaiko L , Chikwembani, S
- Date: 2020
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/160478 , vital:40449 , https://doi.org/10.1016/j.radmeas.2020.106457
- Description: Features of luminescence optically stimulated from natural kunzite using 470 nm blue light are reported. Preparatory measurements of its X-ray excited radioluminescence and thermoluminescence show that the sample has two main bands centered at 360 nm and 600 nm. The optically stimulated luminescence discussed in this report was monitored in the UV region and is presumed to be the same 360 nm emission that appears in the radioluminescence and thermoluminescence spectra. The glow curve shows at least three peaks at 74, 202, 432 oC for heating at 1 oC and the third one is a composite of two. Only the first two peaks are deduced to contribute most of the optically stimulated luminescence.
- Full Text:
- Date Issued: 2020
Optically stimulated luminescence of ultra-high molecular weight polyethylene: a study of dosimetric features
- Chithambo, Makaiko L, Kalita, Jitumani M
- Authors: Chithambo, Makaiko L , Kalita, Jitumani M
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/110035 , vital:33217 , https://doi.org/10.1016/j.radmeas.2018.06.006
- Description: We report the dosimetric features of ultra-high molecular weight polyethylene (UHMWPE) using luminescence optically stimulated using 470 nm blue light. Samples irradiated to between 1 and 1000 Gy produces luminescence that increases with irradiation dose to produce a linear dose response between 1 and 1000 Gy. The sample was determined not to be affected by pre-dose in tests using a pre-dose of 4000 Gy. This characteristic precludes the need for elaborate background erasing routines typical of dosimetry experiments. The signal has good reproducibility. We used this property to test recovery of ‘unknown’ doses with encouraging results. It was observed that luminescence can also be stimulated using 870 nm infrared light. The dose response, fading, pre-dose effect and the ability to optically stimulate luminescence from the polymer is discussed in terms of curing involving free-radicals.
- Full Text: false
- Date Issued: 2018
- Authors: Chithambo, Makaiko L , Kalita, Jitumani M
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/110035 , vital:33217 , https://doi.org/10.1016/j.radmeas.2018.06.006
- Description: We report the dosimetric features of ultra-high molecular weight polyethylene (UHMWPE) using luminescence optically stimulated using 470 nm blue light. Samples irradiated to between 1 and 1000 Gy produces luminescence that increases with irradiation dose to produce a linear dose response between 1 and 1000 Gy. The sample was determined not to be affected by pre-dose in tests using a pre-dose of 4000 Gy. This characteristic precludes the need for elaborate background erasing routines typical of dosimetry experiments. The signal has good reproducibility. We used this property to test recovery of ‘unknown’ doses with encouraging results. It was observed that luminescence can also be stimulated using 870 nm infrared light. The dose response, fading, pre-dose effect and the ability to optically stimulate luminescence from the polymer is discussed in terms of curing involving free-radicals.
- Full Text: false
- Date Issued: 2018
Orthopaedic grade ultra–high molecular weight polyethylene: some features of the main thermoluminescence glow curve
- Authors: Chithambo, Makaiko L
- Date: 2006
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/125499 , vital:35789 , https://doi.10.1093/rpd/nci661
- Description: Thermoluminescence (TL) characteristics of orthopaedic–grade ultra–high molecular weight polyethylene have been investigated between 20 and 200_C. The TL at 1_C s_1 consists of two glow curves, a weaker intensity peak at 115_C and the main peak at 70_C, studied in this work. TL intensity increases with beta irradiation but with a dose–response influenced by heating rate. On the other hand, the peak maximum is affected by both irradiation and repeated use of a sample. The glow curve shifts to higher temperatures with increase in heating rate but only slightly so with change in beta irradiation dose, properties suggestive of first-order kinetics. Kinetic analysis for activation energy and order of kinetics, based on the discrete trap model, produce somewhat conflicting results. Whereas qualitative analysis of peak symmetry show that first-order kinetics apply, geometrical analysis of the peak shape suggests that the order of kinetics might be other than first-order. Values of activation energy evaluated using the initial rise method were found to be dose dependent and for a given beta dose are in agreement with calculations from peak shape and initial rise methods but less so with results from variable heating rate method.
- Full Text:
- Date Issued: 2006
- Authors: Chithambo, Makaiko L
- Date: 2006
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/125499 , vital:35789 , https://doi.10.1093/rpd/nci661
- Description: Thermoluminescence (TL) characteristics of orthopaedic–grade ultra–high molecular weight polyethylene have been investigated between 20 and 200_C. The TL at 1_C s_1 consists of two glow curves, a weaker intensity peak at 115_C and the main peak at 70_C, studied in this work. TL intensity increases with beta irradiation but with a dose–response influenced by heating rate. On the other hand, the peak maximum is affected by both irradiation and repeated use of a sample. The glow curve shifts to higher temperatures with increase in heating rate but only slightly so with change in beta irradiation dose, properties suggestive of first-order kinetics. Kinetic analysis for activation energy and order of kinetics, based on the discrete trap model, produce somewhat conflicting results. Whereas qualitative analysis of peak symmetry show that first-order kinetics apply, geometrical analysis of the peak shape suggests that the order of kinetics might be other than first-order. Values of activation energy evaluated using the initial rise method were found to be dose dependent and for a given beta dose are in agreement with calculations from peak shape and initial rise methods but less so with results from variable heating rate method.
- Full Text:
- Date Issued: 2006
Phosphorescence of orthopaedic–grade ultra high molecular weight polyethylene
- Authors: Chithambo, Makaiko L
- Date: 2008
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/125617 , vital:35801 , https://doi.10.1002/pssc.200776802
- Description: Isothermal luminescence decay curves have been measured from orthopaedic–standard ultra high molecular weight polyethylene between 35 and 70 ˚C on the rising edge of the main glow peak at 70 ˚C. Preparatory peak-shape analysis of the temperature-resolved glow peak at 70 ˚C measured at 1 ˚C s–1 gave a geometrical factor close to 0.5 suggestive of second order kinetics for both the isothermal and thermally stimulated luminescence. The results of analysis of the phosphorescence of transformed monotonic-to-peak isothermal decay curves are also second order, as is the conclusion from thermoluminescence glow-curve de-convolution. All methods of analysis give an activation energy of about 0.7 eV.
- Full Text:
- Date Issued: 2008
- Authors: Chithambo, Makaiko L
- Date: 2008
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/125617 , vital:35801 , https://doi.10.1002/pssc.200776802
- Description: Isothermal luminescence decay curves have been measured from orthopaedic–standard ultra high molecular weight polyethylene between 35 and 70 ˚C on the rising edge of the main glow peak at 70 ˚C. Preparatory peak-shape analysis of the temperature-resolved glow peak at 70 ˚C measured at 1 ˚C s–1 gave a geometrical factor close to 0.5 suggestive of second order kinetics for both the isothermal and thermally stimulated luminescence. The results of analysis of the phosphorescence of transformed monotonic-to-peak isothermal decay curves are also second order, as is the conclusion from thermoluminescence glow-curve de-convolution. All methods of analysis give an activation energy of about 0.7 eV.
- Full Text:
- Date Issued: 2008
Photoluminescence and thermoluminescence properties of BaGa2O4
- Noto, L L, Poelman, D, Orante-Barrón, V R, Swart, H C, Mathevula, Langutani E, Nyenge, R, Chithambo, Makaiko L, Mothudi, B M, Dhlamini, M S
- Authors: Noto, L L , Poelman, D , Orante-Barrón, V R , Swart, H C , Mathevula, Langutani E , Nyenge, R , Chithambo, Makaiko L , Mothudi, B M , Dhlamini, M S
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116037 , vital:34292 , https://doi.org/10.1016/j.physb.2017.07.059
- Description: Rare–Earth free luminescent materials are fast becoming important as the cost of rare earth ions gradually increases. In this work, a Rare–Earth free BaGa2O4 luminescent compound was prepared by solid state chemical reaction, which was confirmed to have a single phase by X-ray Diffraction. The Backscattered Electron image and Energy Dispersive X-ray spectroscopy maps confirmed irregular particle and homogeneous compound formation, respectively. The Photoluminescence spectrum displayed broad emission between 350 to 650 nm, which was deconvoluted into two components. The photoluminescence excitation peak was positioned at 254 nm, which corresponds with the band-to-band position observed from the diffuse reflectance spectrum. The band gap was extrapolated to 4.65 ± 0.02 eV using the Kubelka-Munk model. The preliminary thermoluminescence results indicated that the kinetics involved were neither of first nor second order. Additionally, the activation energy of the electrons within the trap centres was approximated to 0.61 ± 0.01 eV using the Initial Rise model.
- Full Text: false
- Date Issued: 2018
- Authors: Noto, L L , Poelman, D , Orante-Barrón, V R , Swart, H C , Mathevula, Langutani E , Nyenge, R , Chithambo, Makaiko L , Mothudi, B M , Dhlamini, M S
- Date: 2018
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/116037 , vital:34292 , https://doi.org/10.1016/j.physb.2017.07.059
- Description: Rare–Earth free luminescent materials are fast becoming important as the cost of rare earth ions gradually increases. In this work, a Rare–Earth free BaGa2O4 luminescent compound was prepared by solid state chemical reaction, which was confirmed to have a single phase by X-ray Diffraction. The Backscattered Electron image and Energy Dispersive X-ray spectroscopy maps confirmed irregular particle and homogeneous compound formation, respectively. The Photoluminescence spectrum displayed broad emission between 350 to 650 nm, which was deconvoluted into two components. The photoluminescence excitation peak was positioned at 254 nm, which corresponds with the band-to-band position observed from the diffuse reflectance spectrum. The band gap was extrapolated to 4.65 ± 0.02 eV using the Kubelka-Munk model. The preliminary thermoluminescence results indicated that the kinetics involved were neither of first nor second order. Additionally, the activation energy of the electrons within the trap centres was approximated to 0.61 ± 0.01 eV using the Initial Rise model.
- Full Text: false
- Date Issued: 2018