Adsorption and separation of platinum and palladium by polyamine functionalized polystyrene-based beads and nanofibers
- Authors: Fayemi, Omolola E , Ogunlaja, Adeniyi S , Kempgens, Pierre F M , Antunes, Edith M , Torto, Nelson , Nyokong, Tebello , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241694 , vital:50961 , xlink:href="https://doi.org/10.1016/j.mineng.2013.06.006"
- Description: Adsorption and separation of platinum and palladium chlorido species (PtCl62- and PdCl42-) on polystyrene beads as well as nanofibers functionalized with ammonium centres based on ethylenediamine (EDA), diethylenetriamine (DETA), triethylenetetramine (TETA) and tris-(2-aminoethyl)amine (TAEA) are described. The functionalized sorbent materials were characterized by microanalysis, SEM, XPS, BET and FTIR. The surface area of the functionalized fibers was in the range 69–241 m2/g while it was 73–107 m2/g for the beads. The adsorption and loading capacities of the sorption materials were investigated using both the batch and column studies at 1 M HCl concentration. The adsorption studies for both PtCl62- and PdCl42- on the different sorbent materials fit the Langmuir isotherm with R2 values >0.99. The highest loading capacity of Pt and Pd were 7.4 mg/g and 4.3 mg/g respectively for the nanofiber sorbent material based on ethylenediamine (EDA) while the beads with ethylenediamine (EDA) gave 1.0 mg/g and 0.2 mg/g for Pt and Pd respectively. Metals loaded on the sorbent materials were recovered by using 3% m/v thiourea solution as the eluting agent with quantitative desorption efficiency under the selected experimental conditions. Separation of platinum from palladium was partially achieved by selective stripping of PtCl62- with 0.5 M of NaClO4 in 1.0 M HCl while PdCl42- was eluted with 0.5 M thiourea in 1.0 M HCl. Separation of platinum from iridium and rhodium under 1 M HCl concentration was successful on triethylenetriamine (TETA)-functionalized Merrifield beads. This material (M-TETA) showed selectivity for platinum albeit the low loading capacity.
- Full Text:
Catalytic oxidation of thioanisole using oxovanadium (IV)‐functionalized electrospun polybenzimidazole nanofibers
- Authors: Walmsley, Ryan S , Hlangothi, Percy , Litwinski, Christian , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/242083 , vital:51000 , xlink:href="https://doi.org/10.1002/app.38067"
- Description: Polybenzimidazole fibers, with an average diameter of 262 nm, were produced by the process of electrospinning. These fibers were used as a solid support material for the immobilization of oxovanadium(IV) which was achieved via a reaction with vanadyl sulfate. The oxovanadium(IV)-functionalized nanofibers were used as heterogeneous catalysts for the oxidation of thioanisole under both batch and pseudo-continuous flow conditions with great success. Under batch conditions near quantitative oxidation of thioanisole was achieved in under 90 min, even after four successive catalytic reactions. Under continuous conditions, excellent conversion of thioanisole was maintained throughout the period studied at flow rates of up to 2 mLh−1. This study, therefore, proposes that electrospun polybenzimidazole nanofibers, with their small diameters, impressive chemical and thermal stability, as well as coordinating benzimidazole group, may be a desirable support material for immobilization of homogeneous catalysts.
- Full Text:
Oxovanadium (IV)-containing poly (styrene-co-4′-ethenyl-2-hydroxyphenylimidazole) electrospun nanofibers for the catalytic oxidation of thioanisole
- Authors: Walmsley, Ryan S , Litwinski, Christian , Antunes, Edith M , Hlangothi, Percy , Hosten, Eric C , McCleland, Cedric , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241665 , vital:50959 , xlink:href="https://doi.org/10.1016/j.molcata.2013.07.018"
- Description: The catalytic fibers have been fabricated by the electrospinning of a copolymer of styrene and 2-(2′-hydroxy-4′-ethenylphenyl)imidazole {p(ST-co-VPIM)} followed by a reaction with a methanolic vanadyl solution to afford the oxovanadium(IV)-containing poly(styrene-co-4′-ethenyl-2-hydroxyphenylimidazole) fibers {p(ST-co-VPIM)-VO fibers}. The relationship between polymer concentration and fiber diameter was investigated, and at high concentration (20 wt%) the fibers were quite large (average diameter of 3.8 μm) but as the concentration was reduced fibers of much lower diameter were produced (0.6 μm using 8 wt%). The BET surface area for p(ST-co-VPIM) fibers (0.6 μm diameter) was 47.9 m2 g−1 and functionalization of p(ST-co-VPIM) with vanadyl resulted in an increase in surface area to 60.7 m2 g−1 for p(ST-co-VPIM)-VO. The presence of vanadyl was confirmed by XPS and EPR. The EPR spectral analyses depicted complex speciation of vanadium within these polymer supports. These catalytic fibers were applied under batch and continuous flow conditions for the catalytic oxidation of thioanisole using hydrogen peroxide. The continuous flow method gave excellent and constant conversion throughout the 10 h period studied. The leaching of vanadium from the fiber support was 4% over the 10 h period indicating a significant stability of the material.
- Full Text:
The development of catalytic oxovanadium (IV)-containing microspheres for the oxidation of various organosulfur compounds
- Authors: Ogunlaja, Adeniyi S , Khene, Samson M , Antunes, Edith M , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241783 , vital:50969 , xlink:href="https://doi.org/10.1016/j.apcata.2013.05.004"
- Description: The development of poly[allylSB-co-EGDMA] beads containing a tetradentate ligand was achieved via suspension polymerization. The catalyst poly[allylSB-co-EGDMA]-VO was synthesized by reacting VIVOSO4 with poly[allylSB-co-EGDMA]. XPS and EPR were used to confirm the presence of vanadium (V4+) on the beads. The synthesized catalyst (poly[allylSB-co-EGDMA]-VO) was found to have a BET surface area of 22 m2 g−1 and porosity of 135 Å, with the atomic force microscopy (AFM) showing more insight on the porous nature of the beads. Oxidation of thiophene (TH), benzothiophene (BT), dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) was carried out using tert-butyl hydroperoxide (t-BuOOH) as oxidant. An overall conversion of 60%, 82%, 98% and 87% was achieved for thiophene (TH), benzothiophene (BT), dibenzothiophene (DBT) and 4,6 dimethyldibenzothiophene (4,6-DMDBT) respectively at higher (t-BuOOH) to substrate ratio and at a temperature of 40 °C. The efficient oxidation of the various organosulfur compounds presents potential for the possible application of this catalyst in oxidative desulfurization (ODS) of crude oil.