Effects of annealing on the structural and optical properties of nanostructured TiO2
- Talla, Assane, Urgessa, Zelalem
- Authors: Talla, Assane , Urgessa, Zelalem
- Date: 2023-12
- Subjects: Titanium dioxide , Nanostructured materials , Nanotubes
- Language: English
- Type: Doctorial theses , text
- Identifier: http://hdl.handle.net/10948/62655 , vital:72907
- Description: In this thesis, the structural, morphological and optical properties of titanium dioxide (TiO2) are investigated. Titanium dioxide (TiO2) nanotubes are prepared by anodic oxidation of titanium foil. The as-anodised samples are thermally annealed at various temperatures in nitrogen, air, oxygen and vacuum. The purpose is to study how the annealing conditions affect the properties of the nanostructures, including the anatase to rutile phase transformation. In all annealing atmospheres, except in vacuum, the dominant phase is found to be anatase when annealing is performed up to 600 oC. Above 700 oC the rutile phase becomes dominant. The anatase phase is stable above 600 oC in vacuum and does not evolve significantly up to 900 oC. The morphologies of the tubes tend to deteriorate with increased annealing temperature, in nitrogen, air and oxygen atmospheres, due to sintering effects. However, the integrity of the nanotubes is maintained up to 900 oC in vacuum. The photoluminescence (PL) spectra suggest mainly the presence of oxygen vacancies and self-trapped excitons, with respective emission bands around 2.5 eV and 2.3 eV. The results show that both the annealing temperature and atmosphere strongly influence the crystalline and optical properties of the TiO2 nanotubes. In addition, the phase transformation from anatase to rutile for samples annealed in an oxygen-rich environment is investigated in detail. Complementary structural information obtained from transmission electron microscopy and Raman analysis for oxygen-annealed samples reveals that the nucleation of the rutile phase starts from the titanium substrate and then propagates along the tubes. The results provide suitable annealing conditions to control the phase content and morphology of anodic TiO2 nanotubes. The PL characteristics of bulk crystalline anatase TiO2, namely virgin and hydrogen-annealed at 600 oC for 1 h, are studied. The low temperature PL spectra at 5.5 K shows near band edge (NBE) emissions with two dominant lines ascribed to shallow donor bound exciton and possibly free to bound recombination. The two main transitions are assisted by optical phononmodes. Temperature-dependent PL measurements performed on these anatase crystals reveal that the donor bound exciton is stable below 90 K. Hydrogen trapped in oxygen vacancies is proposed to be the shallow donor. In addition, two activation processes are involved for the thermal quenching of donor bound excitons. The total activation energy is found to correlate well with the localisation energy of the bound exciton. Site-selective PL spectra obtained from anodic TiO2 tubes reveals that the luminescence of the nanostructures depends on the morphology. The result shows unusual near-band edge emission (NBE) for these structures, which is rarely observed in indirect band gap TiO2. , Thesis (PhD) -- Faculty of Science, School of Biomolecular and Chemical Sciences, 2023
- Full Text:
- Date Issued: 2023-12
- Authors: Talla, Assane , Urgessa, Zelalem
- Date: 2023-12
- Subjects: Titanium dioxide , Nanostructured materials , Nanotubes
- Language: English
- Type: Doctorial theses , text
- Identifier: http://hdl.handle.net/10948/62655 , vital:72907
- Description: In this thesis, the structural, morphological and optical properties of titanium dioxide (TiO2) are investigated. Titanium dioxide (TiO2) nanotubes are prepared by anodic oxidation of titanium foil. The as-anodised samples are thermally annealed at various temperatures in nitrogen, air, oxygen and vacuum. The purpose is to study how the annealing conditions affect the properties of the nanostructures, including the anatase to rutile phase transformation. In all annealing atmospheres, except in vacuum, the dominant phase is found to be anatase when annealing is performed up to 600 oC. Above 700 oC the rutile phase becomes dominant. The anatase phase is stable above 600 oC in vacuum and does not evolve significantly up to 900 oC. The morphologies of the tubes tend to deteriorate with increased annealing temperature, in nitrogen, air and oxygen atmospheres, due to sintering effects. However, the integrity of the nanotubes is maintained up to 900 oC in vacuum. The photoluminescence (PL) spectra suggest mainly the presence of oxygen vacancies and self-trapped excitons, with respective emission bands around 2.5 eV and 2.3 eV. The results show that both the annealing temperature and atmosphere strongly influence the crystalline and optical properties of the TiO2 nanotubes. In addition, the phase transformation from anatase to rutile for samples annealed in an oxygen-rich environment is investigated in detail. Complementary structural information obtained from transmission electron microscopy and Raman analysis for oxygen-annealed samples reveals that the nucleation of the rutile phase starts from the titanium substrate and then propagates along the tubes. The results provide suitable annealing conditions to control the phase content and morphology of anodic TiO2 nanotubes. The PL characteristics of bulk crystalline anatase TiO2, namely virgin and hydrogen-annealed at 600 oC for 1 h, are studied. The low temperature PL spectra at 5.5 K shows near band edge (NBE) emissions with two dominant lines ascribed to shallow donor bound exciton and possibly free to bound recombination. The two main transitions are assisted by optical phononmodes. Temperature-dependent PL measurements performed on these anatase crystals reveal that the donor bound exciton is stable below 90 K. Hydrogen trapped in oxygen vacancies is proposed to be the shallow donor. In addition, two activation processes are involved for the thermal quenching of donor bound excitons. The total activation energy is found to correlate well with the localisation energy of the bound exciton. Site-selective PL spectra obtained from anodic TiO2 tubes reveals that the luminescence of the nanostructures depends on the morphology. The result shows unusual near-band edge emission (NBE) for these structures, which is rarely observed in indirect band gap TiO2. , Thesis (PhD) -- Faculty of Science, School of Biomolecular and Chemical Sciences, 2023
- Full Text:
- Date Issued: 2023-12
Synthesis and characterization of titanium dioxide nanotubes on fluorine-doped tin oxide (FTO) glass substrate using electro-anodization technique
- Zinya, Simcelile https://orcid.org/0000-0001-5864-0957
- Authors: Zinya, Simcelile https://orcid.org/0000-0001-5864-0957
- Date: 2017-12
- Subjects: Titanium dioxide , Nanotubes , Nanostructured materials
- Language: English
- Type: Master's theses , text
- Identifier: http://hdl.handle.net/10353/23979 , vital:62201
- Description: One-dimensional (1-D) titanium dioxide nanotubes (TNTs) have attracted much attention as a promising alternative electrode material for dye sensitized solar cell (DSSC). As compared to the randomly packed and disordered TiO2 nanoparticles (TNPs) network with numerous particle-particle interfaces, TNTs prove to have fascinating features than make them suitable candidates in DSSCs. Well-structured TNTs arrays are of great potential among the various types of 1D TiO2 nano-materials owing to their superior electron transport properties with limited grain boundaries. Vectorial transport of photon generated electrons along the TNTs has been reported to lead to higher charge mobility which is crucial for improvement of DSSC performances. In this work, highly adhesive titanium films were deposited on functional substrates (FS) using radio frequency (RF) sputtering technique at a sputtering output power of 1kW, operating pressure of 1.5 Pa and at a deposition temperature of 200 °C to obtain a thickness of 10 μm under an inert argon atmosphere. The duration period for sputter coating 10 μm thickness of titanium film layer was 122 minutes with sputter rate for titanium target of about 82 nm per minutes. Subsequently, the RF sputtered titanium films were anodized with 0.5 wt. percent ammonium fluoride + 0.35 wt. percent deionised water and 96 wt. percent glycerol electrolyte solution at room temperature at 60 V for 72 hours. The resulting TNTs on functional substrates (TNTs-FS) were subjected to thermal treatment at 350 °C, 450 °C, 550 °C and 650 °C for 3 hours under oxygen atmosphere. The effect of annealing temperature on the morphological, and structural properties have been scrutinized. The as prepared and thermally treated TNTs-FS were characterized using scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD) and Confocal Raman Spectroscopy (CRS). SEM and HRTEM techniques were employed to confirm the presence of the TNTs-FS and also to study the structural-morphology of the TNTs as the annealing temperature increases. SEM revealed improvement in morphology with increase in sample annealing temperature, even at high temperatures such as 650 °C with no collapsing and sintering of the TNTs-FS occurring. SEM images revealed TNTs-FS with pore diameter sizes in the range between 85-170 nm. This is in compliance with HRTEM analysis, which revealed smooth and straight tube walls and improved surface morphology with increase in annealing temperature. In addition HRTEM images revealed pore diameter of TNTs-FS in the range between 85-165 nm. Furthermore, HRTEM revealed lattice fringes of 0.351, 0.352 and 0.353 nm between the neighbouring lattice fringes. All corresponding to (101) planes of anatase phase TNTs at different annealing temperatures (350-650 °C). The crystallographic structure of TNTs-FS was characterized by XRD measurements after thermal treatment at 350 °C, 450 °C, 550 °C and 650 °C. The XRD pattern revealed peaks in the wide angle range of 2θ (20° < 2θ > 80°) discovered at 29.43°, 45.10°, 56.52°, 63.5°, 64.92° and 74.81° corresponding to the planes (101), (112), (200), (105), (211) and (204) crystalline structures of the anatase TNTs. The intensity of the peaks increased with increasing annealing temperature. The strong sharp peaks indicate the large quantities and higher degrees of crystallinity of anatase phase of the TNTs. CRS Large Area Scan (LAS) and Depth profiling (DP) were employed to evaluate the crystallinity and phase distribution of TNTs-FS thermally treated at different temperatures. CRS LAS in the XY direction of TNTs-FS revealed the presence of differently crystallized anatase phases of TiO2 with Raman vibrational modes of 159.38 cm-1 (Eg), 208.37 cm-1 (Eg), 399.67 cm-1 (B1g), 514.25 cm-1 (A1g) and 641.58 cm-1 (Eg) for the samples annealed at 350 °C. The effect of annealing temperature on TiO2 phase evolution was meticulously evaluated using CRS for TNTs-FS for the samples annealed at 350 °C, 450 °C, 550 °C and 650 °C. The FWHM was estimated from CRS and decreases with increasing annealing temperature resulting in increasing crystallinity. Increase in anatase FWHM and anatase peak intensity implies higher degree of crystallinity and increasing crystallite sizes were also confirmed by XRD. Growing of titanium dioxide on functional substrates one novel contribution towards the fabrication of efficient electrode materials for solar cell development. Our method of characterizing TNTs-FS from a large area scan along the surface of the samples and depth profiling along the TNTs tube walls using confocal Raman spectroscopy prove to be a pivotal step in the development of efficient photoelectrode materials of the solar devices. , Thesis (MSc) -- Faculty of Science and Agriculture, 2017
- Full Text:
- Date Issued: 2017-12
- Authors: Zinya, Simcelile https://orcid.org/0000-0001-5864-0957
- Date: 2017-12
- Subjects: Titanium dioxide , Nanotubes , Nanostructured materials
- Language: English
- Type: Master's theses , text
- Identifier: http://hdl.handle.net/10353/23979 , vital:62201
- Description: One-dimensional (1-D) titanium dioxide nanotubes (TNTs) have attracted much attention as a promising alternative electrode material for dye sensitized solar cell (DSSC). As compared to the randomly packed and disordered TiO2 nanoparticles (TNPs) network with numerous particle-particle interfaces, TNTs prove to have fascinating features than make them suitable candidates in DSSCs. Well-structured TNTs arrays are of great potential among the various types of 1D TiO2 nano-materials owing to their superior electron transport properties with limited grain boundaries. Vectorial transport of photon generated electrons along the TNTs has been reported to lead to higher charge mobility which is crucial for improvement of DSSC performances. In this work, highly adhesive titanium films were deposited on functional substrates (FS) using radio frequency (RF) sputtering technique at a sputtering output power of 1kW, operating pressure of 1.5 Pa and at a deposition temperature of 200 °C to obtain a thickness of 10 μm under an inert argon atmosphere. The duration period for sputter coating 10 μm thickness of titanium film layer was 122 minutes with sputter rate for titanium target of about 82 nm per minutes. Subsequently, the RF sputtered titanium films were anodized with 0.5 wt. percent ammonium fluoride + 0.35 wt. percent deionised water and 96 wt. percent glycerol electrolyte solution at room temperature at 60 V for 72 hours. The resulting TNTs on functional substrates (TNTs-FS) were subjected to thermal treatment at 350 °C, 450 °C, 550 °C and 650 °C for 3 hours under oxygen atmosphere. The effect of annealing temperature on the morphological, and structural properties have been scrutinized. The as prepared and thermally treated TNTs-FS were characterized using scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD) and Confocal Raman Spectroscopy (CRS). SEM and HRTEM techniques were employed to confirm the presence of the TNTs-FS and also to study the structural-morphology of the TNTs as the annealing temperature increases. SEM revealed improvement in morphology with increase in sample annealing temperature, even at high temperatures such as 650 °C with no collapsing and sintering of the TNTs-FS occurring. SEM images revealed TNTs-FS with pore diameter sizes in the range between 85-170 nm. This is in compliance with HRTEM analysis, which revealed smooth and straight tube walls and improved surface morphology with increase in annealing temperature. In addition HRTEM images revealed pore diameter of TNTs-FS in the range between 85-165 nm. Furthermore, HRTEM revealed lattice fringes of 0.351, 0.352 and 0.353 nm between the neighbouring lattice fringes. All corresponding to (101) planes of anatase phase TNTs at different annealing temperatures (350-650 °C). The crystallographic structure of TNTs-FS was characterized by XRD measurements after thermal treatment at 350 °C, 450 °C, 550 °C and 650 °C. The XRD pattern revealed peaks in the wide angle range of 2θ (20° < 2θ > 80°) discovered at 29.43°, 45.10°, 56.52°, 63.5°, 64.92° and 74.81° corresponding to the planes (101), (112), (200), (105), (211) and (204) crystalline structures of the anatase TNTs. The intensity of the peaks increased with increasing annealing temperature. The strong sharp peaks indicate the large quantities and higher degrees of crystallinity of anatase phase of the TNTs. CRS Large Area Scan (LAS) and Depth profiling (DP) were employed to evaluate the crystallinity and phase distribution of TNTs-FS thermally treated at different temperatures. CRS LAS in the XY direction of TNTs-FS revealed the presence of differently crystallized anatase phases of TiO2 with Raman vibrational modes of 159.38 cm-1 (Eg), 208.37 cm-1 (Eg), 399.67 cm-1 (B1g), 514.25 cm-1 (A1g) and 641.58 cm-1 (Eg) for the samples annealed at 350 °C. The effect of annealing temperature on TiO2 phase evolution was meticulously evaluated using CRS for TNTs-FS for the samples annealed at 350 °C, 450 °C, 550 °C and 650 °C. The FWHM was estimated from CRS and decreases with increasing annealing temperature resulting in increasing crystallinity. Increase in anatase FWHM and anatase peak intensity implies higher degree of crystallinity and increasing crystallite sizes were also confirmed by XRD. Growing of titanium dioxide on functional substrates one novel contribution towards the fabrication of efficient electrode materials for solar cell development. Our method of characterizing TNTs-FS from a large area scan along the surface of the samples and depth profiling along the TNTs tube walls using confocal Raman spectroscopy prove to be a pivotal step in the development of efficient photoelectrode materials of the solar devices. , Thesis (MSc) -- Faculty of Science and Agriculture, 2017
- Full Text:
- Date Issued: 2017-12
- «
- ‹
- 1
- ›
- »